Solution-based processing of van der Waals (vdW) one- (1D) and two-dimensional (2D) materials is an effective strategy to obtain high-quality molecular chains or atomic sheets in a large area with scalability. In this work, quasi-1D vdW Ta2Pt3Se8was exfoliated via liquid phase exfoliation (LPE) to produce a stably dispersed Ta2Pt3Se8nanowire solution. In order to screen the optimal exfoliation solvent, nine different solvents were employed with different total surface tensions and polar/dispersive (P/D) component (P/D) ratios. The LPE behavior of Ta2Pt3Se8was elucidated by matching the P/D ratios between Ta2Pt3Se8and the applied solvent, resulting in N-methyl-2-pyrrolidone (NMP) as an optimal solvent owing to the well-matched total surface tension and P/D ratio. Subsequently, Ta2Pt3Se8nanowire thin films are manufactured via vacuum filtration using a Ta2Pt3Se8/NMP dispersion. Then, gas sensing devices are fabricated onto the Ta2Pt3Se8nanowire thin films, and gas sensing property toward NO2is evaluated at various thin-film thicknesses. A 50 nm thick Ta2Pt3Se8thin-film device exhibited a percent response of 25.9% at room temperature and 32.4% at 100 °C, respectively. In addition, the device showed complete recovery within 14.1 min at room temperature and 3.5 min at 100 °C, respectively.

Graphene-based fibers (GFs) have aroused enormous interest in portable, wearable electronics because of their excellent mechanical flexibility, electrical conductivity, and weavability, which make them advantageous for wearable electronic devices. Herein, we report the development of metal binder-free Ti3C2TxMXene/graphene hybrid fibers by a scalable wet-spinning process. These hybrid fibers exhibit excellent mechanical and electrical properties for applications in flexible wearable gas sensors. The synergistic effects of electronic properties and gas-adsorption capabilities of MXene/graphene allow the created fibers to show high NH3gas sensitivity at room temperature. The hybrid fibers exhibited significantly improved NH3sensing response (ΔR/R0= 6.77%) compared with individual MXene and graphene. The hybrid fibers also showed excellent mechanical flexibility with a minimal fluctuation of resistance of ±0.2% and low noise resistance even after bending over 2000 cycles, enabling gas sensing during deformation. Furthermore, flexible MXene/graphene hybrid fibers were woven into a lab coat, demonstrating their high potential for wearable devices. We envisage that these exciting features of 2D hybrid materials will provide a novel pathway for designing next-generation portable wearable gas sensors.