1. Leeches-Inspired Hydrogel-Elastomer Integration Materials.
- Author
-
Feng JF, Chen JL, Guo K, Hou JB, Zhou XL, Huang S, Li BJ, and Zhang S
- Abstract
Inspired by the functions of leeches, for the first time homogeneous materials integrating hydrogels and elastomers were achieved by free radical polymerization. 2-Methoxyethyl acrylate (MEA) was used as elastomer monomer and Pluronics functionalized with vinyl groups acted as cross-linkers to impart the hydrogel property to the materials. The resulting Pluronic/PMEA gels possess a swelling ratio of about 210% and good water-retaining ability. Compression tests of Pluronic/PMEA gels at swelling equilibrium state show a stress up to 1.6 MPa under 85% strain. The gels act as elastomer after dehydration. Uniaxial tensile fracture stress and the elongation reached 1200 kPa and 500%, respectively, and compression stress was above 22 MPa. Furthermore, the Pluronic/PMEA gels also show self-healing properties. Owing to the excellent mechanical performance in both wet and dry conditions, this hydrogel-elastomer integrated material may have potential applications in tissue engineering, soft robotics, and biomedical devices.
- Published
- 2018
- Full Text
- View/download PDF