Search

Micropatterned polymer surfaces, possessing both topographical and chemical characteristics, were prepared on three-dimensional copper tubes and used to capture atmospheric water. The micropatterns mimic the structure on the back of a desert beetle that condenses water from the air in a very dry environment. The patterned coatings were prepared by the dewetting of thin films of poly-4-vinylpyridine (P4VP) on top of polystyrene films (PS) films, upon solvent annealing, and consist of raised hydrophilic bumps on a hydrophobic background. The size and density distribution of the hydrophilic bumps could be tuned widely by adjusting the initial thickness of the P4VP films: the diameter of the produced bumps and their height could be varied by almost 2 orders of magnitude (1-80 μm and 40-9000 nm, respectively), and their distribution density could be varied by 5 orders of magnitude. Under low subcooling conditions (3 °C), the highest rate of water condensation was measured on the largest (80 μm diameter) hydrophilic bumps and was found to be 57% higher than that on flat hydrophobic films. These subcooling conditions are achieved spontaneously in dew formation, by passive radiative cooling of a surface exposed to the night sky. In effect, the pattern would result in a larger number of dewy nights than a flat hydrophobic surface and therefore increases water capture efficiency. Our approach is suited to fabrication on a large scale, to enable the use of the patterned coatings for water collection with no external input of energy.

A novel flexible three-dimensional (3D) architecture of nitrogen and sulfur codoped graphene has been successfully synthesized via thermal treatment of a liquid crystalline graphene oxide-doping agent composition, followed by a soft self-assembly approach. The high temperature process turns the layer-by-layer assembly into a high surface area macro- and nanoporous free-standing material with different atomic configurations of graphene. The interconnected 3D network exhibits excellent charge capacitive performance of 305 F g(-1) (at 100 mV s(-1)), an unprecedented volumetric capacitance of 188 F cm(-3) (at 1 A g(-1)), and outstanding energy density of 28.44 Wh kg(-1) as well as cycle life of 10 000 cycles as a free-standing electrode for an aqueous electrolyte, symmetric supercapacitor device. Moreover, the resulting nitrogen/sulfur doped graphene architecture shows good electrocatalytic performance, long durability, and high selectivity when they are used as metal-free catalyst for the oxygen reduction reaction. This study demonstrates an efficient approach for the development of multifunctional as well as flexible 3D architectures for a series of heteroatom-doped graphene frameworks for modern energy storage as well as energy source applications.

The reaction of nitric oxide (NO) and carbonaceous materials generates nitrogen functionalities on and in graphitic carbons and oxidizes some of the carbon. Here, we have exploited these phenomena to provide a novel route to surface-functionalized multiwalled carbon nanotubes (MWCNTs). We investigated the impacts of NO on the physical and chemical properties of industrially synthesized multiwalled carbon nanotubes to find a facile treatment that increased the specific surface area (SBET) of the MWCNTs by ∼20%, with only a minimal effect on their degree of graphitization. The technique caused less material loss (∼12 wt %) than traditional gas-based activation techniques and grafted some nitrogen functional groups (1.1 at. %) on the MWCNTs. Moreover, we found that Ni nanoparticles deposited on NO-treated MWCNTs had a crystallite size of dNi = 13.1 nm, similar to those deposited on acid-treated MWCNTs (dNi = 14.2 nm), and clearly much smaller than those deposited under the same conditions on untreated MWCNTs (dNi = 18.3 nm).

Herein, we report a solid-state reduction process (in contrast to solution-based approach) by using an environmentally friendly reductant, such as vitamin C (denoted VC), to be directly employed to solid-state graphene oxide (GO) templates to give the highly active rGO architecture with a sheet resistance of as low as 10 Ω sq(-1). In addition, predesigned rGO patterns/tracks with tunable resistivity can be directly "written" on a preprepared solid GO film via the inkjet-printing technique using VC/H2O as the printing-ink. This advanced reduction process allows foreign active materials to be preincorporated into the GO matrix to form quality active composite architectures.

Aligned multiwalled carbon nanotube (CNT) arrays were prepared using chemical vapor deposition of C2H4 on Fe catalyst at 750 °C. CNT array height and alignment depends strongly on the duration of H2 pretreatment, with optimal height and alignment achieved using 10-15 min pretreatment. Small-angle X-ray scattering (SAXS) was used to quantify the alignment, distribution, and size of the CNTs in arrays produced from varying pretreatment times and the results correlated with microscopy measurements. SAXS analysis revealed that the higher section of the CNT arrays exhibited better alignment than the lower section. Combining these insights with transmission electron microscopy measurements of the CNT defects within each array enable a mechanism for the CNT growth to be proposed, where the loss of alignment arises from deformation of the CNTs during their growth. Gas permeation test across densified CNT arrays indicated that the alignment of the CNT array plays an important role in the gas transport, and that the gas diffusion across the well-aligned CNT arrays was enhanced by a factor of ~45, which is much more than that across the poorly aligned CNT arrays, with an enhancement factor of ~8.

Preparation of bismuth vanadate and cerium dioxide (BiVO4/CeO2) nanocomposites as visible-light photocatalysts was successfully obtained by coupling a homogeneous precipitation method with hydrothermal techniques. The BiVO4/CeO2 nanocomposites with different mole ratios were synthesized and characterized by X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). Absorption range and band gap energy, which are responsible for the observed photocatalyst behavior, were investigated by UV-vis diffuse reflectance (UV-vis DR) spectroscopy. Photocatalytic activities of the prepared samples were examined by studying the degradation of model dyes Methylene Blue, Methyl Orange, and a mixture of Methylene Blue and Methyl Orange solutions under visible-light irradiation (>400 nm). Results clearly show that the BiVO4/CeO2 nanocomposite in a 0.6:0.4 mol ratio exhibited the highest photocatalytic activity in dye wastewater treatment.

A highly sensitive and selective dopamine sensor was fabricated with the unique 3D carbon nanotube nanoweb (CNT-N) electrode. The as-synthesised CNT-N was modified by oxygen plasma to graft functional groups in order to increase selective electroactive sites at the CNT sidewalls. This electrode was characterized physically and electrochemically using HRSEM, Raman, FT-IR, and cyclic voltammetry (CV). Our investigations indicated that the O(2)-plasma treated CNT-N electrode could serve as a highly sensitive biosensor for the selective sensing of dopamine (DA, 1 μM to 20 μM) in the presence of ascorbic acid (AA, 1000 μM)., (© 2011 American Chemical Society)