This study explores the ionic dynamics in 2D/3D perovskite solar cells, which are known for their improved efficiency and stability. The focus is on the impact of halide choice in 3D perovskites treated with phenethylammonium halide salts (PEAX, X = Br and I). Our findings reveal that light and heat drive ionic migration in these structures, with PEA+ species diffusing into the 3D film in PEABr-treated samples. Mixed-halide 3D perovskites show halide interdiffusion, with bromine migrating to the surface and iodine diffusing into the film. Cathodoluminescence microscopy reveals localized 2D phases on the 3D perovskite, which become more evenly distributed after thermal treatment. Both PEAX salts enhance the performance of photovoltaic devices. This improvement is attributed to the passivation capabilities of the salts themselves and their respective Ruddlesden−Popper (RP) phases. Annealed PEAI-treated devices show a better balance between efficiency and statistical distribution of photovoltaic parameters.

Interfacial passivation with bulky organic cations such as phenetylammonium iodide has enabled high performance for metal halide perovskite optoelectronic devices. However, the homogeneity of these interfaces and their formation dynamics are poorly understood. We study how Ruddlesden-Popper 2D phases form at a 3D perovskite interface when the 2D precursors are introduced via solution or via vapor. When using vapor deposition, we observe uniform coverage of the capping layer and the formation of a predominantly n = 2 Ruddlesden-Popper phase. In contrast, when using solution deposition, we observe the presence of a mixture of n = 2 and n = 1 in the film and the formation of aggregates of the organic cations. As a result of the better phase purity and uniformity, vapor deposition enables higher median solar cell performance with narrower distribution compared to solution-treated films. This study provides fundamental information that the perovskite community can use to better design capping layers to achieve higher charge extraction efficiencies.