Hydrophobic and breathable nanofiber membranes have attracted considerable attention owing to their applications in various fields. In this study, we fabricated superhydrophobic and breathable nanofiber membranes using solution blow spinning. We optimized the spinning process parameters by analyzing their effects on the structure and properties of the nanofiber membranes. And the nanofiber membranes achieved superhydrophobicity through hydrophobic modification treatment. The average fiber diameter and pore size of the obtained membrane were 0.51 and 13.65 μm, respectively. The membranes exhibited superhydrophobicity, breathability, and mechanical properties: water vapor transmission of 12.88 kg/m

Solution blowing (SB) is a widely reported technology that can be used to fabricate fibers at the micro- and nanoscale. To reveal the fibrous web formation mechanism in SB, we improved our previous melt blowing (MB) model to predict fibrous web structures. Then, we fabricated two samples and simulated the same number of virtual samples in the computer to verify the model. Thereafter, we measured the structural parameters including the fiber diameter, fiber orientation, basis weight, and pore size. Our model provides a good prediction of the fiber orientation and basis weight. However, the predicted fiber diameter was slightly smaller than the measured diameter. The experimental pore size distribution was also different from that in the simulated results. The model provides a virtual fabrication process to reveal a fibrous web formation mechanism and finds a similar distribution of these structural parameters between SB and MB.