FeCrAl alloy is one of the promising cladding materials in the advanced nuclear reactors. Here we compare the irradiation response of the nanolaminate (NL) and coarse-grained (CG) FeCrAl alloys, by performing He ion irradiation followed by in situ Kr ion irradiation in a transmission electron microscope at 450 °C. NL alloy has reduced He bubble induced swelling and decreased the density of dislocation loops in comparison to the CG alloy. The distribution of He bubbles appears to be dependent on misorientation angles of high angle grain boundaries. A new type of nanoprecipitates was identified in the irradiated CG FeCrAl without noticeable chemical segregation. Chemical segregation occurred along the laminate boundaries in the irradiated NL FeCrAl alloy. [Display omitted] [ABSTRACT FROM AUTHOR]

Nanopatterned microstructures in materials can have a profound impact on materials' physical and chemical properties. While voids are typically considered as detrimental defects in irradiated materials, the patterning of nanoscale voids causes the formation of void superlattices and provides a highly efficient mechanism for gas storage. Despite the important applications of nanopatterned defect superlattices, how they degrade under irradiation remains unclear. Here we provide direct observation of the evolution of void superlattices under irradiation and elucidate the interaction of void superlattices with irradiation cascades. We reveal that the instability of void superlattices under irradiation is caused by heterogenous void shrinkage and demonstrate the imperative role of mixed 1D/3D diffusion of self-interstitial atoms and injected inert gas atoms on void shrinkage and void superlattice instability. Understanding the degradation mechanisms of nanopatterned microstructures is essential to designing damage-tolerant materials and broadening their applications in extreme environments. [Display omitted] [ABSTRACT FROM AUTHOR]