Search

An unusual tensile deformation behaviour in the form of a propagating band along the sample gauge was observed in two neutron-irradiated 316 stainless steel samples during room-temperature tests, leading to a combination of high strength and high ductility. These bands were not observed in an unirradiated counterpart. With the help of in situ high-energy synchrotron x-ray diffraction, the phase-specific crystal information was tracked at different deformation levels in each sample. Post-irradiation and post-deformation samples were examined using electron microscopy to characterize various microstructural features. All samples displayed a deformation-induced martensitic phase transformation, which was identified as a second strain-hardening mechanism accompanying the dislocation hardening. The deformation-induced martensitic transformation was rationalized by the effect of applied stress on the effective martensite start temperature. The results showed that the irradiation did not alter the dislocation hardening and the martensitic transformation mechanisms, but the increased yield strength in irradiated materials facilitated the localized phase transformation at the onset of plastic deformation, in contrast to the unirradiated material which required pre-straining. The hardening effect of the martensitic transformation reduced the tendency towards necking and mitigated the loss of ductility in the irradiated material by carrying the deformation in the form of a propagating band. Despite the beneficial effect from the martensitic transformation, this study indicates that this mechanism cannot not be activated at typical operating temperatures of nuclear reactors.

This study characterizes the microstructural evolution of single-phase complex concentrated solid-solution alloy (CSA) compositions under heavy ion irradiation with the goal of evaluating mechanisms for CSA radiation tolerance in advanced fission systems. Three such alloys, Cr18Fe27Mn27Ni28, Cr15Fe35Mn15Ni35, and equimolar NbTaTiV, along with reference materials (pure Ni and E90 for the CrFeMnNi family and pure V for NbTaTiV) were irradiated at 50 K and 773 K with 1 MeV Kr++ ions to various levels of displacements per atom (dpa) using in-situ transmission electron microscopy. Cryogenic irradiation resulted in small defect clusters and faulted dislocation loops as large as 12 nm in face-centered cubic (FCC) CSAs. With thermal diffusion suppressed at cryogenic temperatures, defect densities were lower in all CSAs than in their less compositionally complex reference materials indicating that point defect production is reduced during the displacement cascade stage. High temperature irradiation of the two FCC CSA resulted in the formation of interstitial dislocation loops which by 2 dpa grew to an average size of 27 nm in Cr18Fe27Mn27Ni28 and 10 nm in Cr15Fe35Mn15Ni35. This difference in loop growth kinetics was attributed to the difference in Mn-content due to its effect on the nucleation rate by increasing vacancy mobility or reducing the stacking-fault energy.

Helium bubble formation was examined by scanning/transmission electron microscopy (S/TEM) in Fe-9/10Cr binary alloys and two dispersion strengthened nanostructured alloys (CNA3 and 14YWT containing 5–10 nm diameter carbide and oxide particles, respectively) after ex-situ and in-situ He implantation to ~10,000 appm at 500 to 900 °C. The combination of high-resolution STEM images and electron energy loss spectroscopy (EELS) revealed that the Y-Ti-O nanoparticles in 14YWT were uniformly distributed and exhibited a one-to-one relationship for bubble attachment to the nanoclusters. In the in-situ experiment at 900 °C, grain boundary cracking was severe in the Fe-10Cr model alloy, but not in the nanostructured alloys. From 500 to 900 °C, the bubble size generally increased with increasing irradiation temperature, while the bubble density decreased with increasing temperature. At the same temperatures, the bubble size in the implanted materials was in the order of Fe-9/10Cr > CNA3 > 14YWT, while the bubble density showed the opposite order. The observed bubble number densities for the nanostructured alloys are comparable to the nanoparticle density, suggesting that the nanoparticles in both alloys were effective in trapping He. Our results indicate that very high He concentrations can be managed in nanostructured alloys by sequestering the helium into smaller bubbles (which leads to a lower volume swelling value) and to shield He from the grain boundaries. This can be attributed to the much higher sink strength associated with the nanoclusters or the He trapping ability between different types of nanoclusters.

The attractive mechanical properties and superior resistance to void-swelling make ferritic/martensitic alloys a promising structural material for advanced nuclear reactors. However, one anomaly that has intrigued researchers for more than 50 years is the proportion of two types of dislocation loops in Fe and Fe-Cr alloys with Burger vectors b=½ and b= . Although the possible mechanisms responsible for the presence of 〈100〉 loops continue to be the subject of intense modeling studies, there remains incomplete experimental understanding of fundamental irradiation processes in Fe(Cr) alloys. Here, the dose dependence of the irradiation-induced microstructural evolution was examined from 0 to 20 displacement per atom (dpa) in high purity Fe and Fe-10Cr during simultaneous dual-beam (1 MeV Kr + 10 appm He/dpa) irradiation at 435 °C. We experimentally revealed that the mechanism for the formation of 〈100〉 loops may not follow the conventional simple dislocation reaction between two ½ loops. Real-time dynamic formation and evolution of defects including black dot loops, loop coarsening, loop decoration, network dislocations, and cavities were demonstrated. Several results indicated that the addition of Cr and He could impede dislocation loop motion. The evolution of the defect size/density and relative fraction of ½ vs 〈100〉 loops were quantitatively summarized. With increasing dose, ½ loops became the dominant type of loop in both materials. Notably, 〈100〉 loops were predominantly observed near grain boundaries only for pure Fe, while arrays of nanoscale black dot defects composing the 〈100〉 loop strings were observed in plenty in Fe-10Cr.

In situ irradiations with 1 MeV Kr ions at 50~613 K up to a fluence of 6.25 × 1014 ions/cm2 (~1.25 displacements per atom, dpa) have been performed on pre-aged dilute Cu-0.9%Co, Cu-0.9%Fe and Cu-0.8%Cr alloys containing uniform matrix dispersions of coherent precipitates in order to study the effects of initial precipitate sink strength, damage dose and irradiation temperature on radiation-induced coherency loss of precipitates. Coherent precipitates with different point defect sink strengths (2πNd, where N and d are the precipitate density and diameter) were used in this work to examine potential differences in atomic relaxation during absorption of point defects. In all cases, irradiation to low doses (