Search

Understanding the stability of irradiation-induced voids in materials is important for engineering material's swelling behavior under irradiation. In-situ TEM offers a spatial and temporal resolution that is suitable for investigating the evolution of voids under irradiation. However, the in-situ videos have often been too large to be analyzed manually, leaving the valuable data underutilized. We developed a deep learning-based semantic segmentation model to consistently study the growth and shrinkage of voids in nickel under 1 MeV krypton ion irradiation at various temperatures from 525 °C to 650 °C. With a foil thickness near 100 nm and ion flux of 6.3 × 1011 ions⋅ cm−2⋅s−1, the pre-existing voids, which were created beforehand by irradiation at 600 °C to 0.5 dpa, shrank at low temperatures and grew at high temperatures under irradiation, where the transition occurred at 575 °C (∼0.5 T M). The observed stability transition provided new insight for the shrinkage mechanism of voids under irradiation. In addition, an annealing experiment on nickel, previously irradiated at 600 °C to 3 dpa, was performed sequentially at 650 °C to 720 °C to reveal the shrinkage rate of void as a function of temperature and void size. The advantage of combining computer vision and in-situ TEM to obtain comprehensive void evolution was demonstrated. [Display omitted] [ABSTRACT FROM AUTHOR]

Fe and Fe-Cr (Cr = 10–16 at.%) specimens were neutron-irradiated at 300 °C to 0.01, 0.1 and 1 dpa. The TEM observations indicated that the Cr significantly reduced the mobility of dislocation loops and suppressed vacancy clustering, leading to distinct damage microstructures between Fe and Fe-Cr. Irradiation-induced dislocation loops in Fe were heterogeneously observed in the vicinity of grown-in dislocations, whereas the loop distribution observed in Fe-Cr is much more uniform. Voids were observed in the irradiated Fe samples, but not in irradiated Fe-Cr samples. Increasing Cr content in Fe-Cr results in a higher density, and a smaller size of irradiation-induced dislocation loops. Orowan mechanism was used to correlate the observed microstructure and hardening, which showed that the hardening in Fe-Cr can be attributed to the formation of dislocation loops and α′ precipitates. [ABSTRACT FROM AUTHOR]

In situ irradiations with 1 MeV Kr ions at 50~613 K up to a fluence of 6.25 × 1014 ions/cm2 (~1.25 displacements per atom, dpa) have been performed on pre-aged dilute Cu-0.9%Co, Cu-0.9%Fe and Cu-0.8%Cr alloys containing uniform matrix dispersions of coherent precipitates in order to study the effects of initial precipitate sink strength, damage dose and irradiation temperature on radiation-induced coherency loss of precipitates. Coherent precipitates with different point defect sink strengths (2πNd, where N and d are the precipitate density and diameter) were used in this work to examine potential differences in atomic relaxation during absorption of point defects. In all cases, irradiation to low doses (<~1 dpa) was very effective at inducing loss of precipitate coherency. At low sink strengths (~1013 m−2), loss of precipitate coherency could be induced for doses ~0.01 dpa. This suggests there might be an efficient preferential medium-range strain-induced bias for absorption of interstitial defects due to tensile strains emanating from the undersized precipitates, which induces relatively rapid loss of coherency at low precipitate sink strengths. High precipitate sink strength (~1014 m−2) conditions were relatively resistant to the radiation-induced loss of coherency (requiring higher doses approaching ~1 dpa) and this might be due to nearly equal numbers of interstitial and vacancy defects arriving at the precipitate interface for such high sink strength conditions. The precipitate coherency loss was observed to have a weak dependence on irradiation temperature. Molecular dynamics simulations confirm a strong effect of precipitate sink strength on the probability of interstitial absorption at precipitates. [Display omitted] [ABSTRACT FROM AUTHOR]

This study characterizes the microstructural evolution of single-phase complex concentrated solid-solution alloy (CSA) compositions under heavy ion irradiation with the goal of evaluating mechanisms for CSA radiation tolerance in advanced fission systems. Three such alloys, Cr 18 Fe 27 Mn 27 Ni 28 , Cr 15 Fe 35 Mn 15 Ni 35 , and equimolar NbTaTiV, along with reference materials (pure Ni and E90 for the CrFeMnNi family and pure V for NbTaTiV) were irradiated at 50 K and 773 K with 1 MeV Kr++ ions to various levels of displacements per atom (dpa) using in-situ transmission electron microscopy. Cryogenic irradiation resulted in small defect clusters and faulted dislocation loops as large as 12 nm in face-centered cubic (FCC) CSAs. With thermal diffusion suppressed at cryogenic temperatures, defect densities were lower in all CSAs than in their less compositionally complex reference materials indicating that point defect production is reduced during the displacement cascade stage. High temperature irradiation of the two FCC CSA resulted in the formation of interstitial dislocation loops which by 2 dpa grew to an average size of 27 nm in Cr 18 Fe 27 Mn 27 Ni 28 and 10 nm in Cr 15 Fe 35 Mn 15 Ni 35. This difference in loop growth kinetics was attributed to the difference in Mn-content due to its effect on the nucleation rate by increasing vacancy mobility or reducing the stacking-fault energy. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Nanopatterned microstructures in materials can have a profound impact on materials' physical and chemical properties. While voids are typically considered as detrimental defects in irradiated materials, the patterning of nanoscale voids causes the formation of void superlattices and provides a highly efficient mechanism for gas storage. Despite the important applications of nanopatterned defect superlattices, how they degrade under irradiation remains unclear. Here we provide direct observation of the evolution of void superlattices under irradiation and elucidate the interaction of void superlattices with irradiation cascades. We reveal that the instability of void superlattices under irradiation is caused by heterogenous void shrinkage and demonstrate the imperative role of mixed 1D/3D diffusion of self-interstitial atoms and injected inert gas atoms on void shrinkage and void superlattice instability. Understanding the degradation mechanisms of nanopatterned microstructures is essential to designing damage-tolerant materials and broadening their applications in extreme environments. [Display omitted] [ABSTRACT FROM AUTHOR]