Polyethylene oxide (PEO) based solid polymer electrolytes (SPEs) are incompatible with the 4 V class cathodes such as LiCoO2 due to the limited electrochemical oxidation window of PEO. Herein, a number of binders including commonly used binders PEO, polyvinylidene fluoride (PVDF), and carboxyl‐rich polymer (CRP) binders such as sodium alginate (Na‐alginate) and sodium carboxymethyl cellulose, are studied for application in the 4 V class all‐solid‐state polymer batteries (ASSPBs). The results show ASSPBs with CRP binders exhibit superior cycling performance up to 1000 cycles (60% capacity retention, almost 10 times higher than those with PEO and PVDF binders). Synchrotron‐based X‐ray absorption spectroscopy (XAS), morphology studies and density functional theory studies indicate that, with their carboxyl groups, CRPs can strongly bind the electrode materials together, and work as coating materials to protect the cathode/SPE interface. Cyclic voltammetry studies indicate that CRP binders are more stable at high voltage compared to PEO and PVDF. The stability under high voltage and the coating property of CRP binders contribute to stable cathode/SPE interfaces as disclosed by the X‐ray photoelectron spectroscopy and Co L‐edge XAS results, enabling long cycling life, high performance 4 V class ASSPBs. [ABSTRACT FROM AUTHOR]

Although metallic lithium is regarded as the "Holy Grail" for next‐generation rechargeable batteries due to its high theoretical capacity and low overpotential, the uncontrollable Li dendrite growth, especially under high current densities and deep plating/striping, has inhibited its practical application. Herein, a 3D‐printed, vertically aligned Li anode (3DP‐VALi) is shown to efficiently guide Li deposition via a "nucleation within microchannel walls" process, enabling a high‐performance, dendrite‐free Li anode. Moreover, the microchannels within the microwalls are beneficial for promoting fast Li+ diffusion, supplying large space for the accommodation of Li during the plating/stripping process. The high‐surface‐area 3D anode design enables high operating current densities and high areal capacities. As a result, the Li–Li symmetric cells using 3DP‐VALi demonstrate excellent electrochemical performances as high as 10 mA cm−2/10 mAh cm−2 for 1500 h and 5 mA cm−2/20 mAh cm−2 for 400 h, respectively. Additionally, the Li–S and Li–LiFePO4 cells using 3DP‐VALi anodes present excellent cycling stability up to 250 and 800 cycles at a rate of 1 C, respectively. It is believed that these new findings could open a new window for dendrite‐free metal anode design and pave the way toward energy storage devices with high energy/power density. [ABSTRACT FROM AUTHOR]