Friction stir processing (FSP) was carried out for AE42 Mg alloy resulting in significant grain refinement and uniform dispersion of fine in situ precipitates. The average grain size was 20 μm for the as-cast AE42 alloy, which was refined to 1.5 μm after FSP. Tensile testing revealed significantly higher modulus and yield strength for the friction stir processed (FSPed) specimen with some improvement in ductility. The fractured surface of the as-cast alloy showed ridges, grooves and cracks indicating brittle failure. In contrast, the fractured surface of FSPed specimen showed fine dimples, characteristic of ductile failure. Nano-indentation was used to analyze the variation of hardness and modulus across the nugget zone of the FSPed specimen. FSPed specimen demonstrated greater strain-hardening tendency compared to the as-cast alloy. Enhancing the mechanical properties of Mg alloys can result in substantial cost savings across a number of industries and have wide economic impact. [ABSTRACT FROM AUTHOR]

Friction stir processing (FSP) of Mg based AE42 alloy was performed under single pass as well as double pass conditions. The evolution of microstructure was investigated using electron back scatter diffraction (EBSD) analysis. EBSD revealed that the grain size and texture varies within the nugget zone of friction stir processed region. The variation of mechanical properties across the nugget region was evaluated using nanoindentation. Hardness and Young's modulus was found to increase along the depth of the friction stir processed specimen. This was attributed to a finer grain structure with increasing depth. The friction stir processed specimen showed higher tendency toward strain hardening compared to as-cast alloy. Understanding microstructure-property relationship paves the way for optimization of FSP conditions and development of advanced functional Mg alloys. [ABSTRACT FROM AUTHOR]