Previous research on iron oxides/hydroxides has focused on the crystalline rather than the amorphous phase, despite that the latter could have superior electrochemical activity due to the disordered structure. In this work, a simple and scalable synthesis route is developed to prepare amorphous FeOOH quantum dots (QDs) and FeOOH QDs/graphene hybrid nanosheets. The hybrid nanosheets possess a unique heterostructure, comprising a continuous mesoporous FeOOH nanofilm tightly anchored on the graphene surface. The amorphous FeOOH/graphene hybrid nanosheets exhibit superior pseudocapacitive performance, which largely outperforms the crystalline iron oxides/hydroxides-based materials. In the voltage range between −0.8 and 0 V versus Ag/AgCl, the amorphous FeOOH/graphene composite electrode exhibits a large specific capacitance of about 365 F g−1, outstanding cycle performance (89.7% capacitance retention after 20 000 cycles), and excellent rate capability (189 F g−1 at a current density of 128 A g−1). When the lower cutoff voltage is extended to −1.0 and −1.25 V, the specific capacitance of the amorphous FeOOH/graphene composite electrode can be increased to 403 and 1243 F g−1, respectively, which, however, compromises the rate capability and cycle performance. This work brings new opportunities to design high-performance electrode materials for supercapacitors, especially for amorphous oxides/hydroxides-based materials. [ABSTRACT FROM AUTHOR]

For building high-energy density asymmetric supercapacitors, developing anode materials with large specific capacitance remains a great challenge. Although Fe2O3 has been considered as a promising anode material for asymmetric supercapacitors, the specific capacitance of the Fe2O3-based anodes is still low and cannot match that of cathodes in the full cells. In this work, a composite material with well dispersed Fe2O3 quantum dots (QDs, ≈2 nm) decorated on functionalized graphene-sheets (FGS) is prepared by a facile and scalable method. The Fe2O3 QDs/FGS composites exhibit a large specific capacitance up to 347 F g−1 in 1 m Na2SO4 between -1 and 0 V versus Ag/AgCl. An asymmetric supercapacitor operating at 2 V is fabricated using Fe2O3/FGS as anode and MnO2/FGS as cathode in 1 m Na2SO4 aqueous electrolyte. The Fe2O3/FGS//MnO2/FGS asymmetric supercapacitor shows a high energy density of 50.7 Wh kg−1 at a power density of 100 W kg−1 as well as excellent cycling stability and power capability. The facile synthesis method and superior supercapacitive performance of the Fe2O3 QDs/FGS composites make them promising as anode materials for high-performance asymmetric supercapacitors. [ABSTRACT FROM AUTHOR]