This study focused on the engineering properties of alkali-activated slag (AAS) pastes prepared by mixing an activator consisting of sodium silicate and sodium hydroxide at room temperature. The water-to-slag ratio of AAS paste was kept constant at 0.35 by mass. AAS pastes were prepared using the activator with five different silicate moduli of 1, 1.2, 1.4, 1.6, and 1.8 and three different Na2O contents of 6%, 8%, and 10%. The results showed that both the silicate moduli and Na2O contents had significant effects on the engineering properties of AAS pastes. All the AAS pastes exhibited properties such as fast setting, good workability, and high early compressive strength. The final setting time varied from 9 to 36 min, and the fluidity was in the range of 147–226 mm. The 1 d compressive strength of all the AAS pastes, which could be easily achieved, had values above 55 MPa, whereas the highest strength obtained was 102 MPa with the silicate modulus of 1 and Na2O content of 8% at room temperature. The drying shrinkage increased as the silicate modulus increased. Furthermore, the hydration products and microstructures of AAS pastes were explained according to the microanalysis methods. [ABSTRACT FROM AUTHOR]

Alkali-activated slag (AAS) mortars were prepared using pottery sand as a fine aggregate in a ratio of 1 : 1.75 using a blend of sodium silicate and NaOH as an alkaline activator at room temperature. The effects of sodium oxide content and silicate moduli on the setting time, fluidity, consistency, compressive strength, and drying shrinkage of different AAS mortars were determined. These results revealed that sodium oxide content and silicate modulus had little effect on the setting time and workability of the mortar; however, they did have a significant effect on their mechanical performance and drying shrinkage levels. All the AAS mortars exhibited faster setting times, better workability, and higher early and late compressive strength compared to traditional mortars. Optimum compressive strength was achieved at 93 and 123 MPa after 1 d and 28 d, respectively, using a silicate modulus of 1.2 and Na2O content of 8%. The microstructures of mortars were characterized using scanning electron microscopy with energy dispersive spectrometric (SEM/EDS) and mercury intrusion porosimetry (MIP). These results reveal that AAS mortars containing pottery sand as a fine aggregate may represent a promising building material with improved properties for use in the construction industry. [ABSTRACT FROM AUTHOR]