Layered perovskite oxides A3B2O7 with Ruddlesden–Popper structures have attracted great attention due to their intriguing hybrid improper ferroelectricity. In this work, we prepared high-quality epitaxial Ca3Ti2O7 (CTO) thin films on Nb-SrTiO3 (STO) and Pt–Si substrates by pulsed laser deposition. The epitaxial relationship between the CTO thin film and Nb-STO substrate is [010]CTO//[010]Nb-STO, while the CTO film on Pt–Si is the polycrystalline growth with the preferred orientation of (010). The piezoelectric force microscopy image is attested to the stable existence of ferroelectricity in CTO films at room temperature with different growth patterns. A resistive switching behavior with at least two orders of magnitude is observed in CTO films driven by their ferroelectric polarization reversal. Moreover, a downward self-poling phenomenon is observed in CTO films on different substrates, and the flexoelectric effect induced by the strain gradient is supposed to be the main origin.

Magnetoelectric (ME) coefficient dependence on the bias magnetic field at resonance frequencies for the bi-layered bonded Terfenol-D/Pb(Zr,Ti)O3 composite was investigated. The resonance frequency decreases first and then increases with the bias magnetic field (HDC), showing a “V” shape in the range of 0 ∼ 5 kOe. Below the resonance frequency, the pattern of ME coefficient dependence on the HDC shows a single peak, but splits into a double-peak pattern when the testing frequency increases into a certain region. With increasing the frequency, a divergent evolution of the HDC patterns was observed. Domain motion and ΔE effect combined with magnetostriction-piezoelectric coupling effect were employed to explain this experimental result.