Search

As they degrade and age, concrete structures are susceptible to the development of multiple defects, such as alkali-silica reaction (ASR). ASR forms a gel that occurs over time between alkaline cement paste and reactive, noncrystalline silica in aggregates [1]. With the continuing extension of the life span of nuclear power plants, it is important to monitor the structural integrity of concrete structures after 40+ years. Compression strength, modulus of elasticity, flexural stiffness, shear strength, and tensile strength are performance characteristics susceptible to the development of ASR. Current methods for monitoring for defects and degradation within thick concrete structures require damaging the concrete. Oak Ridge National Laboratory, in collaboration with the University of Pittsburgh, has developed a nondestructive evaluation (NDE) and reconstruction technique that enables deep-image reconstruction of damaged concrete. The frequency-banded synthetic aperture focusing technique (FB-SAFT) is an augmented SAFT reconstruction that segments the time-series data into different frequency bands using wavelets immediately before performing SAFT reconstructions [2]. This paper presents the NDE instrumentation and reconstruction techniques applied to thick-reinforced concrete structures and concludes with preliminary results. [ABSTRACT FROM AUTHOR]

Alkali-silica reaction (ASR) is the chemical reaction that occurs in concrete. It is caused by the interaction of alkalis in Portland cement and silica in aggregates and results in microcracks within the material. This type of damage has been the focus of nondestructive evaluation efforts in recent history, but no work was done on in-situ structures or large-scale samples. To address these limitations, an ultrasonic linear array device, MIRA, was utilized for this research. An experimental investigation was performed on four slabs with various levels of alkali-silica reaction at the Electric Power Research Institute (EPRI) [1]. One-period impulses with a target of 50kHz center frequency were selected in this study. We propose the use of the Hilbert Transform Indicator (HTI) for quantification of ASR damage [2]. A higher HTI value would be indicative of damaged concrete, while a low value represents sound concrete. In general, values below 90 are regarded as an indicator of sound concrete while values above 100 indicate the presence of damage [3]. The ability of the HTI values to distinguish between areas of damaged concrete was evident via the production of color intensity maps. The maps show that the control specimen, was in good condition, while other slabs exhibited higher levels of damage as indicated by the HTI values. It should be noted that extreme damage conditions were not present in any of the slabs. Evaluation of migration-based reconstructions can give a qualitative characterization of large scale or excessive subsurface damage. However, for detection of stochastic damage mechanisms such as freeze-thaw damage, evaluation of the individual time-history data can provide additional information. A comparison of the spatially diverse measurements on several concrete slabs with varying freeze-thaw damage levels is given in this study. Signal characterization scans of different levels of freeze-thaw damage at various transducer spacing is investigated. The results show promise for a SH-wave classification system applicable for nondestructive characterization of freeze-thaw damage conditions. [ABSTRACT FROM AUTHOR]

Oak Ridge National Laboratory (ORNL) comparatively evaluated the ability of a number of NDE techniques to generate an image of the volume of 6.5' X 5.0' X 10" concrete specimens fabricated at the Florida Department of Transportation (FDOT) NDE Validation Facility in Gainesville, Florida. These test blocks were fabricated to test the ability of various NDE methods to characterize various placements and sizes of rebar as well as simulated cracking and non-consolidation flaws. The first version of the ultrasonic linear array device, MIRA [version 1], was one of 7 different NDE equipment used to characterize the specimens. This paper deals with the ability of this equipment to determine subsurface characterizations such as reinforcing steel relative size, concrete thickness, irregularities, and inclusions using Kirchhoff-based migration techniques. The ability of individual synthetic aperture focusing technique (SAFT) B-scan cross sections resulting from self-contained scans are compared with various processing, analysis, and interpretation methods using the various features fabricated in the specimens for validation. The performance is detailed, especially with respect to the limitations and implications for evaluation of a thicker, more heavily reinforced concrete structures. [ABSTRACT FROM AUTHOR]