This work focused on the study of crystallization behavior and thermal stability of degradable poly(butylene succinate) (PBS) and poly(propylene carbonate) (PPC) blends prepared by vane extruder based on elongation force field, which is novel equipment for polymer processing. Dicumyl peroxide (DCP) was applied in this work as compatibilizer for PBS/PPC blend. Crystallization behavior and melting behavior of the blends were investigated by differential scanning calorimetry (DSC) testing. Thermal stability of the blends was studied by thermogravimetric (TG) testing. Furthermore, the melt flow indices (MFI) of the blends were examined by a MFI instrument. The results showed that the crystallization temperature of PBS decreased with the addition of PPC and DCP. The glass transition temperature of PPC increased and the melting temperature of the blend increased with the addition of PPC and DCP, which indicated that the entanglement between the molecular chains of PBS and PPC was enhanced. Thermogravimetric ana...

Poly (lactic acid) (PLA)/Poly (propylene carbonate) (PPC) blends were prepared by vane extruder which is a type of novel polymer processing extruder based on elongation force field. Scanning electron microscope (SEM), differential scanning calorimetry (DSC) and thermogravimetric (TG) were used respectively to analyze the compatibility, the melting behavior and thermal stability properties of PLA/PPC blends affected by the different content of PPC. The results showed that with the increase of the PPC content, the glass transition temperature of PLA was reduced, and the glass transition temperature of PPC was increased, which indicated that PLA and PPC had partial compatibility. The cold crystallization temperature of PLA increased with the increase of the PPC content, which showed that PPC hindered the cold crystallization process of PLA. The addition of PPC had little impact on the melting process of PLA, and the melting temperature of PLA was almost kept the same value. Thermogravimetric analysis showed that the thermal stability of PPC was worse than that of PLA, the addition of PPC reduced the thermal stability of PLA.