Search

In this work, synthesis of β-V2O5 nanorods by solvothermal method was adopted at optimum experimental conditions by varying the concentration of NaOH as 0.5M, 1M, 1.5M and 2M. The obtained products were characterization by following techniques, XRD, RAMAN, FTIR, and FESEM. The XRD results reveal the formation of β-V2O5 nanorods and its crystalline nature was confirmed by its lattice parameters. The Raman analysis shows a peak at 485, 770 and 998 cm−1 corresponds to the vibration of O-V-O bonds. Similarly the FITR peaks appeared at the 530 and 786 cm−1 can be attributed to the symmetric stretching of Metal Oxide (V-O). The morphology and its structure of β-V2O5 nanorods can be analysized by the FESEM techniques and its images shows the formation of β-V2O5 nanorods with different dimensions. The role of concentration of NaOH can be studied by comparing the FESEM micrographs. It is clearly evident from FESEM images as the concentration of NaOH increases from 0.5 M to 2M, the shape and size of the change rapidly and the surface effect results in the mesoporous features on the surface of nanorods. Its note worthy as the concentration of NaOH increases results in the flattening of nanorods could be observed due more of interaction of NaOH precursor solution. [ABSTRACT FROM AUTHOR]

An attempt was made to synthesis the copper doped tin oxide (Cu-SnO2) nanoparticles by adopting different chelating agents (NaOH, KOH and C2H2O4) by Sol-gel process. The synthesized products were characterized by XRD, Photoluminescence (PL), Infra- Red (FTIR) and SEM analysis. The XRD confirms the formation of Cu-SnO2 shows the maximum peak at 33.8° with lattice plane (101). The PL peak at 361 and 382 nm due to the recombination of electron in conduction band to valence band infers the optical properties. The IR spectra correspond to the peak at 551 and 620 cm−1 attributed to the characteristics peak for Cu-SnO2 nanoparticles. The SEM images for all three Cu-SnO2 nanoparticles formed by three chelating agent (NaOH, KOH and C2H2O4) facilitates the formation mechanism and the chelating agent Oxalic acid results in formation of nano flowers with diverse layers orientated in random direction. Further SEM studies reveal that, the Cu-SnO2 nanoparticles formed by oxalic acid could posses high surface area with large number layered structured enables the better electrochemical properties and its applications. [ABSTRACT FROM AUTHOR]

Facile and economically viable one step hydrothermal route was adapted to synthesis SnO2/α-Fe2O3 nanocomposite with and without hexamine (HMT) as surfactant successfully. The formation of SnO2/α-Fe2O3 nanocomposite was confirmed through XRD, Raman, PL and FTIR studies. The presence of well defined XRD diffraction peaks of both SnO2 and α-Fe2O3 revealed the formation SnO2/α-Fe2O3 nanocomposite. The obtained characteristic Raman active (Eg+Eg+Eu+A2u) mode of vibrations confirmed the formation of SnO2/α-Fe2O3 nanocomposite. Photoluminescence study revealed the emission behavior of the product. Metal oxygen vibrations of Fe-O in both octahedral, tetrahedral sites and Sn-O were confirmed by the bands located at 466, 580 and 673 cm−1 respectively through FTIR. The spherical morphology of the product synthesized with and without the surfactant HMT has been revealed by SEM images. The electrochemical behavior of the product was investigated through CV and EIS studies in 1M Na2SO4 electrolyte solution and obtained the highest specific capacitance of 211.25 F/g at 5 mV for the surfactant assisted product. [ABSTRACT FROM AUTHOR]