Search

Despite the great research interest in two‐dimensional metal nanowire networks (2D MNWNs) due to their large specific surface area and abundance of unsaturated coordination atoms, their controllable synthesis still remains a significant challenge. Herein, a microfluidics laminar flow‐based approach is developed, enabling the facile preparation of large‐scale 2D structures with diverse alloy compositions, such as PtBi, AuBi, PdBi, PtPdBi, and PtAuCu alloys. Remarkably, these 2D MNWNs can reach sizes up to submillimeter scale (~220 μm), which is significantly larger than the evolution from the 1D or 3D counterparts that typically measure only tens of nanometers. The PdBi 2D MNWNs affords the highest specific activity for formic acid (2669.1 mA mg−1) among current unsupported catalysts, which is 103.5 times higher than Pt‐black, respectively. Furthermore, in situ Fourier transform infrared (FTIR) experiments provide comprehensive evidence that PdBi 2D MNWNs catalysts can effectively prevent CO* poisoning, resulting in exceptional activity and stability for the oxidation of formic acid. [ABSTRACT FROM AUTHOR]

Direct conversion of methane into value‐added chemicals, such as methanol under mild conditions, is a promising route for industrial applications. In this work, atomically dispersed Rh on TiO2 suspended in an aqueous solution was used for the oxidation of methane to methanol. Promoted by copper cations (as co‐catalyst) in solution, the catalysts exhibited high activity and selectivity for the production of methanol using molecular oxygen with the presence of carbon monoxide at 150 °C with a reaction pressure of 31 bar. Millimole level yields of methanol were reached with the selectivity higher than 99 % using the Rh/TiO2 catalysts with the promotion of the copper cation. CO was the reductive agent to generate H2 from H2O, which led to the formation of H2O2 through the reaction of H2 and O2. Atomically dispersed Rh activated the C−H bond in CH4 and catalyzed the oxidation using H2O2. Copper cations maintained the low‐valence state of Rh. Moreover, copper acted as a scavenger for suppressing the overoxidation, thus leading to the high selectivity of methanol. [ABSTRACT FROM AUTHOR]

A photocatalyst system is generally comprises a catalyst and cocatalyst to achieve light absorption, electron‐hole separation, and surface reaction. It is a challenge to develop a single photocatalyst having all functions so as to lower the efficiency loss. Herein, the active GaN4 site is integrated into a polymeric carbon nitride (CN) photocatalyst (GCN), which displays an excellent H2 production rate of 9904 μmol h−1 g−1. It is 162 and 3.3 times higher than that of CN with the absence (61 μmol h−1 g−1) and presence (2981 μmol h−1 g−1), respectively, of 1.0 wt % Pt. Under light irradiation the electron is injected and stored at the GaN4 site, where the LUMO locates. The HOMO distributes on the aromatic ring resulting in spatial charge separation. Transient photovoltage discloses the electron‐storage capability of GCN. The negative GaN4 promotes proton adsorption in the excited state. The positive adsorption energy drives H2 desorption from GaN4 after passing the electron to the proton. This work opens up opportunities for exploring a novel catalyst for H2 production. [ABSTRACT FROM AUTHOR]

Direct conversion of methane into value‐added chemicals, such as methanol under mild conditions, is a promising route for industrial applications. In this work, atomically dispersed Rh on TiO2 suspended in an aqueous solution was used for the oxidation of methane to methanol. Promoted by copper cations (as co‐catalyst) in solution, the catalysts exhibited high activity and selectivity for the production of methanol using molecular oxygen with the presence of carbon monoxide at 150 °C with a reaction pressure of 31 bar. Millimole level yields of methanol were reached with the selectivity higher than 99 % using the Rh/TiO2 catalysts with the promotion of the copper cation. CO was the reductive agent to generate H2 from H2O, which led to the formation of H2O2 through the reaction of H2 and O2. Atomically dispersed Rh activated the C−H bond in CH4 and catalyzed the oxidation using H2O2. Copper cations maintained the low‐valence state of Rh. Moreover, copper acted as a scavenger for suppressing the overoxidation, thus leading to the high selectivity of methanol. [ABSTRACT FROM AUTHOR]