Search

Aqueous spinning dopes for dry spinning of alumina green fibers were prepared by using basic aluminium chloride Al2(OH)5Cl · 2.5 H2O and SiO2 sol as inorganic components and poly(vinyl alcohol) (PVA) as polymeric organic component. Certain rheological properties of the mixtures are essential to achieve good spinnability at high spinning speeds. The rheology of the dope is influenced by the molecular weight and the degree of hydrolysis of the PVA, as well as by the composition and the concentration of the mixture. For mixtures without SiO2 best results were obtained at a PVA: Al2O3 mass ratio of 18:82 and an Oxide content of about 27 wt.-%. The PVA used has an average molecular weight of 70000 and a degree of hydrolysis of 89%. The dopes were spun to continuous green fibers at speeds up to 500 m/min. The structure and the ageing behaviour of concentrated solutions of basic aluminium chloride has been intensively studied. Wasrige Spinnmassen fur das Trockenspinnen von Aluminiumoxid-Grunfasern wurden hergestellt. Dabei wurden basisches Aluminiumchlorid Al2(OH)5Cl · 2,5 H2O und SiO2-Sol als anorganische Komponenten und Polyvinylalkohol (PVA) als polymere organische Komponente eingesetzt. Bestimmte rheologische Eigenschaften der Mischungen sind essentiell, um eine gute Spinnbarkeit bei hohen Spinngeschwindigkeiten zu erhalten. Die Rheologie der Spinnmassen wird zum einen vom Molekulargewicht und dem Verseifungsgrad des PVA beeinflust und zum anderen von der Zusammensetzung und der Konzentration der Mischung. Fur Mischungen ohne SiO2 wurden die besten Ergebnisse bei einem PVA:Al2O3, Massenverhaltnis von 18:82 und einem Oxidgehalt von ungefahr 27 Gew.-% erzielt. Der verwendete PVA hat ein mittleres Molekulargewicht von 70000 und einen Verseifungsgrad von 89%. Die Spinnmassen wurden mit Spinngeschwindigkeiten von bis zu 500 m/min zu kontinuierlichen Grunfasern versponnen. Die Struktur und das Alterungsverhalten von konzentrierten Losungen von basischem Aluminiumchlorid wurden ausfuhrlich untersucht.

PET and PA 66 fabrics were dyed with different disperse dyes under regular conditions. The dyed fabrics were irradiated with 180 kV electron radiation. It was observed that increasing radiation doses led to increasing total color differences dE if compared to the unirradiated materials. These color differences are mainly caused by two types of reactions. First by the reversible formation of dye radicals, which can be reoxidized (in air) to the original dye molecules, and second by the irreversible reaction of dye molecules with the fiber polymer. The latter reaction causes a permanent change of the color of the fabric, which can be kept low with the proper irradiation conditions. The decision whether or not this change can be tolerated depends on the further use of the textile. PET- und PA 66-Textilien wurden unter normalen Bedingungen mit verschiedenen Dispersionsfarbstoffen gefarbt. Die gefarbten Textilien wurden mit 180 kV Elektronenstrahlung bestrahlt. Es wurde beobachtet, das, verglichen mit den unbestrahlten Materialien, zunehmende Strahlungsdosen zu einer Zunahme des Gesamtfarbabstandes dE fuhrten. Diese Farbunterschiede werden hauptsachlich von zwei Reaktionen verursacht: Erstens von der reversiblen Bildung von Farbstoffradikalen, die (an Luft) wieder zu den Ausgangsfarbstoffen reoxidiert werden konnen und zweitens durch die irreversible Reaktion von Farbstoffmolekulen mit dem Faserpolymeren. Die zweite Reaktion ruft eine permanente Farbanderung des Textils hervor, die bei entsprechenden Bestrahlungsbedingungen klein gehalten werden kann. Die Entscheidung, ob diese Veranderung toleriert werden kann, hangt von der weiteren Verwendung des Textils ab.