Purpose: This study aims to investigate the corrosion inhibitor effect of migrating corrosion inhibitor (MCI) on Q235 steel in high alkaline environment under cathodic polarization. Design/methodology/approach: This study investigated the electrochemical characteristics of Q235 steel with and without MCI by polarization curve and electrochemical impedance spectroscopy. Besides, the surface composition of Q235 steel under different environments was analyzed by X-ray photoelectron spectroscopy. In addition, the migration characteristic of MCI and the adsorption behavior of MCI under cathodic polarization were studied using Raman spectroscopy. Findings: Diethanolamine (DEA) and N, N-dimethylethanolamine (DMEA) can inhibit the increase of Fe(II) in the oxide film of Q235 steel under cathodic polarization. The adsorption stability of DMEA film was higher under cathodic polarization potential, showing a higher corrosion inhibition ability. The corrosion inhibition mechanism of DEA and DMEA under cathodic polarization potential was proposed. Originality/value: The MCI has a broad application prospect in the repair of damaged reinforced concrete due to its unique migratory characteristics. The interaction between MCIs, rebar and concrete with different compositions has been studied, but the passivation behavior of the steel interface in the presence of both the migrating electric field and corrosion inhibitors has been neglected. And it was investigated in this paper. [ABSTRACT FROM AUTHOR]

Purpose: This paper aims to study the effect of chloride concentration on the properties of passive film formed on Q235 steel in simulated concrete pore solutions. Design/methodology/approach: Mott–Schottky analysis and electrochemical impedance spectroscopy were used to study the passive film of Q235 steel in simulated concrete pore solution. X-ray photoelectron spectroscopy was used to analyze the composition of passive film on Q235 steel. Findings: When the chloride concentration is below the chloride threshold value, open circuit potential (OCP) and Rct gradually increases and donor concentration (ND) remains unchanged with the increasing immersion time. When the chloride concentration exceeds chloride threshold value, OCP and Rct decreases after a temporary increase and ND increases. The linear region of the Mott–Schottky curve lost its linearity. The electrochemical process control step is changed from charge transfer control to oxygen diffusion control. As the chloride concentration increases, the FeO content in the passive film increases and the Fe2O3 content decreases. Chloride can destroy the outer layer of passive film and introduce impurities. Originality/value: The effects of chloride and immersion time on the change process of passive films on Q235 steel in simulated concrete pore solution were studied using electrochemical methods. The mechanism of chloride destroying passive film was analyzed. [ABSTRACT FROM AUTHOR]