Abstract: Hydrodechlorination of 4-chlorophenol using Pd/A2O3 as catalyst at mild conditions (30°C, 1atm) was carried out in plain water, buffered (CH3COOH/NaCH3COO, NaH2PO4/Na2HPO4 and NaHCO3/Na2CO3) and alkaline NaOH media at different pH. The highest reaction rate was achieved when the process was carried out at alkaline NaOH solution of pH=8.5. Continuous long term experiments (τ: 5.4kgcat h/mol) were performed in plain water and alkaline medium using Pd/Al2O3 and Pd/AC as catalysts. The former showed an appreciable loss of activity upon time on stream, which was associated with the formation of palladium chloride complexes. However, a residual activity remained practically stable, reaching very similar 4-chlorophenol conversion (36%) in both reaction media. The Pd/AC catalyst maintained a constant activity at a 70% 4-chlorophenol conversion once the steady state was reached. This suggests that the AC supported catalyst is less susceptible to the chloride poisoning produced during the reaction. [Copyright &y& Elsevier]

In this work, polymer-based spherical activated carbon (PBSAC) (dp = 500 μm) has been used as support to synthesize several Pd/PBSAC (1% wt.) catalysts. These catalysts have been tested in the hydrodechlorination (HDC) of 4‐chlorophenol (4-CP) in aqueous phase under ambient-like conditions (30 °C, 1 atm) at [4-CP] 0 = 3.9 mmol L −1 ; [catalyst] 0 = 1 g L −1 and 50 N mL H 2 min −1 . A sequential calcination (200 °C, air atmosphere) − reduction (80 °C, H 2 atmosphere) treatment was required to obtain active HDC catalysts with a convenient proportion of zero-valent and electrodefficient Pd species. This catalyst allowed to achieve complete conversion of 4-CP in 90 min reaction time, giving rise to phenol as main reaction product. An expanded kinetic model accounting for both consecutive reaction and sorption processes was used to successfully fit the experimental data. The values obtained for the effective rate constant of 4-CP disappearance (3.26–10.88 × 10 −4 s −1 ) and apparent activation energy (31.6 kJ mol −1 ) were close to the previously reported for powdered supported Pd catalysts. Remarkably, the catalyst showed a high stability in long-term continuous application (100 h on stream). [ABSTRACT FROM AUTHOR]