• The competitive adsorption between SO 2 and NO x is the main reason for the decrease of activity in low temperature. • The formation and consumption of ABS reach a dynamic equilibrium, making the negative effect on the SCR activity limited. • The accumulation of ferric sulfate species enhances the surface acidity and promotes E-R pathway, further facilitating the activity. • The higher the temperature, the more SO 4 2− accumulated, and the rapider climbing rate of the catalytic activity. SO 2 poisoning of NH 3 -SCR catalysts at low temperature (< 300 °C) is still an austere challenge. In this work, γ-Fe 2 O 3 was taken as a model catalyst and the effect of reaction temperature on the catalytic activity in the presence of SO 2 were fully revealed. SO 2 introduction has no negative effect on the activity at 300 °C, which gradually improves with the extension of time. While for 225−275 °C, the activity decreases firstly and then increases slowly. The formatted sulfate species inhibits the adsorption of NO x , cuts off L-H reaction pathway and leads to the initial decline. While the deposited ammonium bisulfate (ABS) can be consumed continuously by NO + O 2 , implying the formation and consumption of ABS have reached a dynamic equilibrium. Moreover, the formation of ferric sulfate species results in the enhancement of surface acidity, which leads to the promotion of the E-R reaction pathway and further facilitates the increase of activity. [ABSTRACT FROM AUTHOR]

Modifying CeO 2 with acid sites is a common strategy for designing efficient catalysts for the selective catalytic reduction of NO x by NH 3 (NH 3 -SCR of NO x). However, the effect of acid metal oxide modification on the SO 2 resistance of CeO 2 has not been well revealed. In this work, it was found that the SO 2 resistance of CeO 2 modified with several acid metal oxides (i.e. , MoO 3 , WO 3 and Nb 2 O 5), followed an order of Mo/CeO 2 ≥ W/CeO 2 > Nb/CeO 2. Further systematic characterizations revealed that Mo-OH and W-OH on CeO 2 as Brønsted acid sites could better inhibit the SO 2 adsorption and the sulfation of active sites than highly dispersed NbO x mainly as Lewis acid sites because NH 4 + coordinated to Brønsted acid sites could help trap SO 2 to form ammonium sulfates rather than metal sulfates. The findings in this work provided important guidance for the design of efficient catalysts with superior SO 2 resistance performance. [Display omitted] • CeO 2 modified with varying acid metal oxides showed different resistance to SO 2. • Highly dispersed MoO 3 or WO 3 could better shield CeO 2 from SO 2 poisoning than Nb 2 O 5. • Mo and W sites as Brønsted acid sites could better inhibit the SO 2 adsorption on CeO 2. • SO 2 could interact with both highly dispersed Nb 2 O 5 and CeO 2 on Nb/CeO 2. • A strategy for designing efficient catalysts with superior resistance to SO 2 was provided. [ABSTRACT FROM AUTHOR]