Abstract: A graphitic mesoporous carbon (denoted as GMC) was synthesized using resorcinol and formaldehyde as carbon precursors and iron nitrate as a graphitization catalyst. The GMC was characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy (TEM), and nitrogen adsorption. The results show that the GMC has a mesoporous structure and a high surface area of 403 m2 g−1, and particularly, a well-defined graphitic framework. Using the GMC as the support, a PtRu/GMC was synthesized to act as an electrocatalyst for the methanol oxidation reaction (MOR). A counterpart with Vulcan® XC-72 (denoted as XC) as the support was prepared for comparison. TEM images show that PtRu nanoparticles are distributed uniformly on the carbon supports for both electrocatalysts. The electrochemical activity of the PtRu/GMC toward the MOR is slightly higher than that of the PtRu/XC in both half cell and single cell measurements. The 1500h stability test of a single cell suggests that the PtRu/GMC is excellent stable. [Copyright &y& Elsevier]

• Ultrathin 2D metal-organic frameworks decorated with Pt NPs have been fabricated using an ultrasonication-assisted method. • A "win-win" electron decoration effect has been evidenced on the active sites for both ORR and OER. • Remarkable bifunctional catalytic activity towards ORR and OER with ultralow overpotential gap of 665 mV has been demonstrated. • Excellent performance and durability is achieved in the rechargeable Zinc-air battery assembled with the bifunctional catalyst. To meet the increasing demands for highly active electrocatalysts towards oxygen reduction reaction (ORR) and oxygen evolution reaction (OER), here in this work, a new strategy of synergistic nano-architecture design based on Platinum nanoparticles (Pt NPs) and ultrathin two-dimensional (2D) metal-organic frameworks (MOFs) is developed for bifunctional electrochemical catalysts. Compared with commercial Pt/C and RuO 2 catalysts, remarkable enhancements in activity and durability of both oxygen reduction and oxygen evolution reactions are achieved on our PtNPs@MOFs composite materials, with one of the lowest over-potential gaps (E gap) of 665 mV that has ever been reported. The tests on the assembled Zn-air batteries have revealed promising electrocatalytic performance and practical advantage of our new materials as air cathode catalyst. Both experimental results and theoretical study have confirmed the synergistic effect between Pt NPs and MOF nanosheets through a "win-win" electron structural modification, demonstrating the effectiveness of our strategy in developing effective bifunctional oxygen electrocatalysts for various types of electrochemical devices. [ABSTRACT FROM AUTHOR]