Extreme-high-speed laser cladding (EHLA), as a novel surface treatment technique, has attracted great attention because of its high cladding rate and good performance of cladding coatings. However, when depositing coatings with high cracking susceptibility, such as Ni60 coatings, cracks are difficult to avoid. Therefore, an extreme-high-speed laser-induction hybrid cladding technology (EH-LIHC) was innovatively proposed in this study. The effects of different preheating temperatures on the surface morphology, internal defects, microstructure, and mechanical properties of Ni60 coatings that were deposited by EHLA and EH-LIHC were analyzed. The results show that the roughness of the coating deposited by EHLA is 26.228 μm. However, the surface roughness of the coating deposited by EH-LIHC at 400 ℃ decreases to 14.316 μm. Simultaneously, the pores- and cracks-free Ni60 coating was deposited at 400 ℃. The coating dilution rate obviously increases as the preheating temperature rises. When the preheating temperature rises, the size of the grains and precipitates also increases. However, although Fe elemental diffusion is increased, there is no significant effect on the properties of the coating. The hardness of the coating fluctuates between 700 and 900 HV, nearly three times that of the substrate. As the preheating temperature rises, the coating's wear mechanism shifts from abrasive to abrasive and adhesive wear, and eventually back to abrasive wear. The improvement of wear resistance of the Ni60 coating deposited at 400 ℃ was mainly attributed to its high hardness and uniform and dense microstructure. The proposed EH-LIHC technique provides a promising method for the efficient deposit of crack-free coatings with good properties. [ABSTRACT FROM AUTHOR]