Search

Single-walled carbon nanotube (SWCNT) is generally used as a networked structure in the fabrication of a field-effect transistor (FET) since it is known that one-third of SWCNT is electrically metallic and the remains are semiconducting. In this case, the presence of metallic paths by metallic SWCNT (m-SWCNT) becomes a significant technical barrier which hinders the networks from achieving a semiconducting behavior, resulting in a low on/off ratio. Here, we report on an easy method of controlling the on/off ratio of a FET where semiconducting SWCNT (s-SWCNT) and m-SWCNT constitute networks between source and drain electrodes. A FET with SWCNT networks was simply sonicated under water to control the on/off ratio and network density. As a result, the FET having an almost metallic behavior due to the metallic paths by m-SWCNT exhibited a p-type semiconducting behavior. The on/off ratio ranged from 1 to 9.0 × 104 along sonication time. In addition, theoretical calculations based on Monte-Carlo method and circuit simulation were performed to understand and explain the phenomenon of a change in the on/off ratio and network density by sonication. On the basis of experimental and theoretical results, we found that metallic paths contributed to a high off-state current which leads to a low on/off ratio and that sonication formed sparse SWCNT networks where metallic paths of m-SWCNT were removed, resulting in a high on/off ratio. This method can open a chance to save the device which has been considered as a failed one due to a metallic behavior by a high network density leading to a low on/off ratio.

Black phosphorus (BP) has been proposed as a future optoelectronic material owing to its direct bandgap with excellent electrical performances. However, oxygen (O 2 ) and water (H 2 O) molecules in an ambient condition can create undesired bubbles on the surface of the BP, resulting in hampering its excellent intrinsic properties. Here, we report the electrical degradation pattern of a mechanically exfoliated BP field–effect transistor (FET) in terms of the channel and contact, separately. Various electrical parameters such as the threshold voltage ( V TH ), carrier mobility ( μ ), contact resistance ( R CT ) and channel resistance ( R CH ) are estimated by the Y function method ( YFM ) with respect to time (up to 2000 min). It is found that R CT reduces and then, increases with time; whereas, the behavior of R CH is vice versa in ambient conditions. We attribute these effects to oxygen doping at the contact and the surface oxidation effects on the surface of the BP, respectively.

Hexagonal boron nitride (h-BN) is a ceramic compound which is thermally stable up to 1000 °C in air. Due to this, it is a very challenging task to etch h-BN under air atmosphere at low temperature. In this study, we report that h-BN flakes can be easily etched by oxidation at 350 °C under air atmosphere in the presence of transition metal (TM) oxide. After selecting Co, Cu, and Zn elements as TM precursors, we simply oxidized h-BN sheets impregnated with the TM precursors at 350 °C in air. As a result, microscopic analysis revealed that an etched structure was created on the surface of h-BN flakes regardless of catalyst type. And, X-ray diffraction patterns indicated that the air oxidation led to the formation of Co 3 O 4 , CuO, and ZnO from each precursor. Thermogravimetric analysis showed a gradual weight loss in the temperature range where the weight of h-BN flakes increased by air oxidation. As a result of etching, pore volume and pore area of h-BN flakes were increased after catalytic oxidation in all cases. In addition, the surface of h-BN flakes became highly active when the h-BN samples were etched by Co 3 O 4 and CuO catalysts. Based on these results, we report that h-BN flakes can be easily oxidized in the presence of a catalyst, resulting in an etched structure in the layered structure.