Search

Ammonium dihydrogen phosphate (ADP) is a nitrogen-phosphorus-based inorganic flame retardant that is environmentally friendly and non-toxic. Wood treated with ADP has enhanced thermal stability and flame retardancy. Compounding ADP with Acid Red 3R dye further improves the decorative effect of the wood on the basis of excellent flame retardancy, resulting in a kind of dyeing and flame retardant multifunctionalized wood. Single-factor tests were designed to investigate the effects of flame retardant concentration, dye concentration, temperature, and time on three evaluation indexes: dye-uptake, color difference, and oxygen index, respectively. Through SEM and FTIR analysis, it was found that after the wood was simultaneously treated with flame retardant and dye, the two additives were aggregated in the grain pores of the cell wall by a simple physical combination. They did not undergo a chemical reaction. TG analysis showed that fire-retardant dyed wood had good thermal stability, which can delay the thermal degradation of wood and increase the residual charcoal rate of wood. XRD showed that the crystallinity of fire-retardant dyed wood increased compared to untreated wood. Through cone calorimetric test, it is found that flame retardant dyed veneer had excellent flame retardancy.

To enhance the synergistic effect of phosphorus (P) and nitrogen (N) on flame retardant property, four different phytic acid-based NP flame retardants (FR-PAN) were manufactured using phytic acid and urea with various molar ratios, ranging from 1:3 to 1:12. The FR-PAN water solution was used to impregnate poplar wood under vacuum condition, and the thermal degradation performance of the FR-PAN treated wood were investigated. Compared to untreated wood, the PAN-6 (molar ratio is 1:6) group showed a reduction of 57.1% in total heat release and 80.0% in total smoke release. In the combustion, due to the introduction of P and N, FR-PAN generates O=P/C-O/C-P/C-N bonds, forming highly graphitized char residues, which effectively isolate the entry of oxygen and heat and play a good protective role in the condensed phase. Morphological and chemical analysis of the residual char layer revealed that the introduction of P and N elements formed a more stable hybrid structure, significantly improving the thermal stability of the char layer. Among them, the PAN-6 group exhibited the highest char layer stability, indicating optimal synergistic effects of nitrogen and phosphorus under these conditions.

To enhance the synergistic effect of phosphorus (P) and nitrogen (N) on flame retardant property, four different phytic acid-based NP flame retardants (FR-PAN) were manufactured using phytic acid and urea with various molar ratios, ranging from 1:3 to 1:12. The FR-PAN water solution was used to impregnate poplar wood under vacuum condition, and the thermal degradation performance of the FR-PAN treated wood were investigated. Compared to untreated wood, the PAN-6 (molar ratio is 1:6) group showed a reduction of 57.1% in total heat release and 80.0% in total smoke release. In the combustion, due to the introduction of P and N, FRPAN generates O=P/C-O/C-P/C-N bonds, forming highly graphitized char residues, which effectively isolate the entry of oxygen and heat and play a good protective role in the condensed phase. Morphological and chemical analysis of the residual char layer revealed that the introduction of P and N elements formed a more stable hybrid structure, significantly improving the thermal stability of the char layer. Among them, the PAN-6 group exhibited the highest char layer stability, indicating optimal synergistic effects of nitrogen and phosphorus under these conditions. [ABSTRACT FROM AUTHOR]