Search

Abstract Background The aim of this study was to compare the radiopacity of calcium silicate cements using a digital imaging method. Methods Four calcium silicate cements, NeoMTA 2, OrthoMTA, ProRoot MTA, and Biodentine, were used in this study. Disk-shaped samples were prepared from each material and placed on a plexiglass plate. An aluminum step-wedge was placed alongside the samples on a digital sensor and exposed to 70 kVp and 8 mA from 30 cm away for 0.32 s. The greyness values ​​of the tested materials were measured digitally with the system software and compared with those of the step-wedge to determine the equivalent aluminum thickness. Results The radiopacity values, expressed in equivalent millimetres of aluminum, of the studied materials ProRoot MTA, OrthoMTA, NeoMTA 2, and Biodentine were 4.32 ± 0.17 mm Al, 3.92 ± 0.09 mm Al, 3.83 ± 0.07 mm Al, and 2.29 ± 0.21 mm Al, respectively. Statistically significant differences were found between the mean radiographic density values of the tested materials (p

Background: The aim of this study was to compare the radiopacity of calcium silicate cements using a digital imaging method. Methods: Four calcium silicate cements, NeoMTA 2, OrthoMTA, ProRoot MTA, and Biodentine, were used in this study. Disk-shaped samples were prepared from each material and placed on a plexiglass plate. An aluminum step-wedge was placed alongside the samples on a digital sensor and exposed to 70 kVp and 8 mA from 30 cm away for 0.32 s. The greyness values ​​of the tested materials were measured digitally with the system software and compared with those of the step-wedge to determine the equivalent aluminum thickness. Results: The radiopacity values, expressed in equivalent millimetres of aluminum, of the studied materials ProRoot MTA, OrthoMTA, NeoMTA 2, and Biodentine were 4.32 ± 0.17 mm Al, 3.92 ± 0.09 mm Al, 3.83 ± 0.07 mm Al, and 2.29 ± 0.21 mm Al, respectively. Statistically significant differences were found between the mean radiographic density values of the tested materials (p < 0.05). Conclusion: ProRoot MTA was the most radiopaque root canal filling material among the tested materials. All materials, except Biodentine, were found to be compliant with the minimum radiopacity requirements of ISO 6876 and ADA 57 standards. [ABSTRACT FROM AUTHOR]

Abstract Background After reparation of root perforations with calcium silicate-based cements (CSBC), the surface of the material is expected to be exposed to root canal irrigants (RCI) while resuming the root canal treatment. Methods The aim of this study was to compare the effect of exposure to a mixture of sodium hypochlorite (NaOCl) and etidronic acid (HEBP) or other irrigants on the Push Out Bond Strength (POBS) of CSBC after two different setting times. 240 root slices 1 mm thick were obtained from single-rooted human teeth. A 1.4 mm diameter perforation was performed on each slice and filled with Biodentine (BD) or ProRoot MTA (PMTA). After 1 or 21 days they were exposed to 17% ethylenediaminetetraacetic acid, 5.25% NaOCl, a mixture of 5.25% NaOCl and 9% HEBP (NaOCl + HEBP) or saline (n = 15) and submitted to a push-out test. POBS results were analysed with ANOVA and Tukey tests. Results BD showed higher POBS than PMTA after 1 day (p

Background: After reparation of root perforations with calcium silicate-based cements (CSBC), the surface of the material is expected to be exposed to root canal irrigants (RCI) while resuming the root canal treatment. Methods: The aim of this study was to compare the effect of exposure to a mixture of sodium hypochlorite (NaOCl) and etidronic acid (HEBP) or other irrigants on the Push Out Bond Strength (POBS) of CSBC after two different setting times. 240 root slices 1 mm thick were obtained from single-rooted human teeth. A 1.4 mm diameter perforation was performed on each slice and filled with Biodentine (BD) or ProRoot MTA (PMTA). After 1 or 21 days they were exposed to 17% ethylenediaminetetraacetic acid, 5.25% NaOCl, a mixture of 5.25% NaOCl and 9% HEBP (NaOCl + HEBP) or saline (n = 15) and submitted to a push-out test. POBS results were analysed with ANOVA and Tukey tests. Results: BD showed higher POBS than PMTA after 1 day (p <.05). After 21 days no differences were found between materials. After 1 day exposure to NaOCl + HEBP resulted in higher POBS, compared to the other irrigants (p <.05). Conclusion: POBS results are influenced by the cement, the setting time and the exposure to irrigants. [ABSTRACT FROM AUTHOR]