Search

This study evaluated the three-year lifespan of the bond to dentin of experimental self-etch adhesives containing benzodioxole derivatives - 1,3-benzodioxole (BDO) and piperonyl alcohol (PA) - as co-initiator alternative to amines. Adhesive resins were formulated using Bis-GMA, TEGDMA, HEMA, camphorquinone and different co-initiators: BDO, PA or ethyl 4-dimethylamino benzoate (EDAB - amine). An experimental selfetch primer was used to complete the two-step, self-etch adhesive system. Clearfil SE Bond (CSE) was used as commercial reference. Bond strength to human dentin was assessed by microtensile bond strength (µTBS) test, and failure mode was classified. Morphology of the dentin bonding interface was assessed via scanning electron microscopy (SEM). Irrespective of the dental adhesives evaluated, µTBS was higher after 24 hours compared with that after 1.5 and 3 years (p = 0.001). However, adhesives with BDO and PA as co-initiators showed significantly higher bond strength than the bonding resin with EDAB (p = 0.002), independent of the time evaluated. The commercial adhesive CSE showed similar bond strength compared with the other groups (p = 0.05). Mixed failures were mainly observed after 24 hours, while adhesive failures were more frequently observed after 1.5 and 3 years. No notable differences in homogeneity and continuity along the bonded interfaces were detected among the materials in the SEM analysis. In conclusion, benzodioxole derivatives are feasible alternative coinitiators to tertiary amine in camphorquinone-based self-etching dental adhesive formulations. [ABSTRACT FROM AUTHOR]

This study evaluated the shear bond strength (SBS) of self-adhesive resin cements (SARCs) to dentin and their physical-chemical properties. Five commercial SARCs were evaluated [SmartCem®2 - DENTSPLY (SC2); BisCem® - Bisco (BC); SeT PP® - SDI (SeT); Relyx U100® - 3M ESPE (U100) and YCEM® SA - Yller (YCEM)]. The SARCs were evaluated for SBS to dentin (n = 10) after 24 h, 6 months, and 12 months. The dentin demineralization caused by acidic monomers was observed by SEM, and pH-neutralization of eluate was observed for 24 h. Degree of conversion (DC), rate of polymerization (Rp), flexural strength (FS), and elastic modulus (E) were evaluated. Immediate SBS of SC2, SET, U100, and YCEM were statistically higher than that of BC (p < 0.001). After 12 months, all SARCs showed reduced SBS values and U100 showed values similar to those of SET and YCEM, and higher than those of BC and SC2 (p = 0.001). Demineralization pattern of SARCs was similar. At 24h, all SARCs showed no differences in the pH-value, except BC and U100 (p < 0.001). YCEM showed the highest Rp. U100, YCEM, and SC2 showed statistically higher FS (p<0.001) and E (p < 0.001) when compared with SET and BC. U100 and YCEM showed the best long-term bonding irrespective of the storage period. A significant reduction in SBS was found for all groups after 12 months. SBS was not shown to be correlated with physical-chemical properties, and appeared to be material-dependent. The polymerization profile suggested that an increased time of light activation, longer than that recommended by manufacturers, would be necessary to optimize DC of SARCs. [ABSTRACT FROM AUTHOR]

A randomized, double-blind, split-mouth clinical trial was performed compared the desensitizing efficacy of the resin-modified glass ionomer cement (GIC) ClinproTM XT (3M ESPE, Minnesota, USA) and the conventional GIC Vidrion R (SS White, Gloucester, UK) in a 6-month follow-up. Subjects were required to have at least two teeth with dentin hypersensitivity. Teeth were divided at random into 2 groups, one group received Clinpro XT and the other conventional GIC Vidrion R. Treatments were assessed by tactile and air blast tests using Visual Analogue Scale (VAS) at baseline, after 20 minutes, and at 7, 15, 21, 30, 90 and 180 days post-treatment. Twenty subjects (152 teeth) were included. Both tests (tactile and air blast) showed a significant reduction of dentin hypersensitivity immediately after the application of Vidrion R and Clinpro XT (20 min). VAS scores obtained along the 6-month follow-up were statistically lower when compared to initial rates (p < 0.05). Both GIC were able to reduce dentin hypersensitivity up to 6-month post-treatment period without statistically significant differences among them (p > 0.05). Both cements provided satisfactory results in long-term dental sensitivity reduction. [ABSTRACT FROM AUTHOR]

This study investigated the impact of 'storage condition' and 'period of storage' on selected physico-mechanical properties and fracture reliability of a resin-based composite (RBC). Specimens, prepared from a nanofilled RBC (Filtek Z350 XT; 3M ESPE), underwent tests for degree of conversion (DC), flexural strength (σ), flexural modulus (E), and hardness. The specimens were initially grouped into dry storage at 37°C or wet storage in distilled water at 37°C. Subsequently, they were further divided into four subgroups based on the period of storage: 6, 24, 72, or 168 hours. Specimens tested immediately after preparation served as control. Data analysis employed two-way ANOVA and Weibull analysis (α = 5%). Compared to the control, an increase in DC was observed only after 72 hours of dry storage; σ showed higher values after both dry and wet storage, regardless of the storage period (except for the group wet-stored for 168 hours); E increased with dry storage for at least 24 hours or wet storage for 72 hours; and hardness increased after dry storage for at least 24 hours or wet storage for up to 72 hours. The Weibull modulus remained unchanged under any of the distinct storage conditions. Dry storage resulted in greater characteristic strength than the control, whereas wet storage contributed to higher strength values only at shorter periods (up to 24 hours). Overall, the inherent properties of RBCs with a similar composition to that tested in this study may change with varying storage conditions and periods.

A randomized, double-blind, split-mouth clinical trial was performed compared the desensitizing efficacy of the resin-modified glass ionomer cement (GIC) ClinproTM XT (3M ESPE, Minnesota, USA) and the conventional GIC Vidrion R (SS White, Gloucester, UK) in a 6-month follow-up. Subjects were required to have at least two teeth with dentin hypersensitivity. Teeth were divided at random into 2 groups, one group received Clinpro XT and the other conventional GIC Vidrion R. Treatments were assessed by tactile and air blast tests using Visual Analogue Scale (VAS) at baseline, after 20 minutes, and at 7, 15, 21, 30, 90 and 180 days post-treatment. Twenty subjects (152 teeth) were included. Both tests (tactile and air blast) showed a significant reduction of dentin hypersensitivity immediately after the application of Vidrion R and Clinpro XT (20 min). VAS scores obtained along the 6-month follow-up were statistically lower when compared to initial rates (p < 0.05). Both GIC were able to reduce dentin hypersensitivity up to 6-month post-treatment period without statistically significant differences among them (p > 0.05). Both cements provided satisfactory results in long-term dental sensitivity reduction.