Search

Ionic conductive hydrogels have been widely applied in sensors, energy storage and soft electronics recently. However, most of the polyvinyl alcohol (PVA) based ionic hydrogels are mainly fabricated by soaking the hydrogels in high concentration electrolyte solution which can induce the waste of electrolyte and solvent. Herein, we have designed cellulose nanofibrils (CNF) and ZnSO4 reinforced PVA based hydrogels through a one-pot simple freezing-thawing method at low ZnSO4 concentration without any soaking process. Furthermore, the hydrogel with 0.4% CNF exhibited stress up to 0.79 MPa (242% strain) and high ionic conductivity of 0.32 S m−1 (0.07 M ZnSO4). Moreover, hydrogel sensor displayed high linear gauge factor 1.70 (0–200% strain), excellent stability, durability and reliability. The integrated hydrogel sensor also showed excellent sensor performance for human motion monitoring. This work provides a new prospect for the design of cellulose reinforced conductive hydrogels via a facile method.

γ-Valerolactone (GVL), a biomass-derived green chemical, offers an environmentally responsible solvent for conversion of lignocellulose to high value-added chemicals. Herein, we report a two-step process for directly producing cellulosic residual, furfural and lignin from Miscanthus × giganteus (M. × giganteus) bypassing the isolation of xylose, which exhibits promising advantage in energy reduction. The optimized pretreatment (100 mM FeCl

We prepared super-hydrophobic nanocellulose films using a non-toxic octadecylamine/polydopamine system. Octadecylamine, a low surface energy material, was used to provide hydrophobic alkyl long chains. Polydopamine was produced by dopamine under alkaline conditions, creating an adhesive substance, which reinforced the hydrophobic long chains and increased the surface roughness of nanocellulose. The effects of reagent concentration, reaction temperature, and reaction time on hydrophobicity were then investigated. The results showed that with a 1:1 mass ratio of nanocellulose to octadecylamine, and reacting at 60 °C for 4 h, the contact angle of the obtained composite membrane reached 168.2°. Scanning electron microscope images revealed that the modified nanocellulose had a smaller particle size and more uniform distribution, which effectively improved the hydrophobicity of the nanocellulose. Thus, the green preparation of superhydrophobic films with high-temperature resistance and wear resistance was realized, which contributed to the high-value utilization of nanocellulose.

γ-Valerolactone (GVL), a biomass-derived green chemical, offers an environmentally responsible solvent for conversion of lignocellulose to high value-added chemicals. Herein, we report a two-step process for directly producing cellulosic residual, furfural and lignin from Miscanthus × giganteus (M. × giganteus) bypassing the isolation of xylose, which exhibits promising advantage in energy reduction. The optimized pretreatment (100 mM FeCl3 at 160 °C for 60 min) induced significant xylan removal (98.4%), resulting in rugged fibre surface, thus leading to the peak cellulose conversion of 99.3%. Furfural yield in the second step reached to 76.6% after 100 mM FeCl3 catalyzed GVL/H2O treatment at 180 °C for 10 min without addition of any chemical. The extracted lignin showed representative structure (such as β-O-4′, β-β′ linkages) and medium molecular weight (4275.5 g/mol). 79.6% of furfural can be recovered by distillation. This study proposes a systematic and energy efficient approach for maximizing biomass utilization.

The hemicellulose, cellulose and lignin were directly separated from corn stalk, and their liquefaction processes were investigated via acid-catalyzed solvolysis treatment with 1,2-propylene glycol (PG) and diethylene glycol (DEG) to produce bio-oil and residues. The main components, functional groups and organics structure of bio-oil were analyzed by the FTIR, 1H-NMR, 13C-NMR, GCMS, and TGA. It was found that there had a similar tendency in the liquefaction processes of cellulose, hemicellulose and lignin. Corn stalk and its biomass components were degraded and formed plentiful low-molecular polymers by acid catalysis, prior to polymers were converted into corresponding PG/DEG-derivatives. Finally, low-molecular weight soluble substances and insoluble residues were generated by decomposition and polymerization. Additionally, more than 80% compounds' carbon number in four bio-oils was below 25. The residues were mostly stemmed from macromolecules produced by degradation products and PG/DEG or re-polymerization between degraded small molecules.