Search

Enhanced electrochemical reduction of CO 2 to syngas on CuZnOCNT catalyst. • Copper doping on ZnO shifts the ECR activity towards CO formation closer to the top of the volcano. • The optimal amount of copper is around 20 at% for CO formation from electrochemical reduction of CO 2. • Higher amount of Cu doping leads to metallic Cu segregation, resulting in higher H 2 evolution activity. • The 14Cu86ZnO/CNT catalyst shows best performance in terms of syngas (1:1 ratio) production at -0.9 V, better than Ag foil. Electrochemical CO 2 reduction is a promising method for the production of CO 2 neutral fuels and chemicals from renewable electricity. ZnO supported on CNT is a low-cost electro catalyst that can produce syngas from CO 2 and H 2 O. A rational catalyst design strategy for further improvement of the ZnO/CNT catalyst is to dope with copper to strengthen the binding energy of the CO intermediate, which could improve the activity. In this work, a series of CuZnO/CNT catalysts with intimate Cu and Zn contact and various Cu loadings are prepared. By varying the copper content we show that the synergy of copper and zinc improves the activity for CO formation, and the optimal copper content is 20 at%. On hydrogen evolution, the addition of copper has a two-fold effect. This reaction is enhanced by the reduced ZnO particle size obtained when copper is added, but at similar particle sizes of ZnO, a suppression is observed with increasing copper content as CO evolution is enhanced. Stability tests showed that pure ZnO phase is more stable than metallic copper on ZnO. Compared with polycrystalline silver, the CuZnO/CNT catalysts are more active for syngas formation at a useful CO: H 2 composition. This work demonstrates that the viability of DFT based rational design of electrochemical CO 2 reduction catalyst. By varying CuZnO composition as well as crystallite size, one is able to tune the electrochemical reduction activity towards CO and H 2 , and therefore achieve desired syngas ratio. [ABSTRACT FROM AUTHOR]

• The reducibility and structural stability of LaMO 3 (M = Sc - Cu) are examined. • The first four LaMO 3 perovskites have very high oxygen vacancy formation energies. • The maximum possible oxygen deficiency in LaMO 3 (M = Mn - Ni) is 0.5. • LaCuO 3 can lose one lattice oxygen atom per formula unit before it is deactivated. Periodic density functional theory calculations have been performed to examine the effect of oxygen deficiency on the structural stability of Lanthanum-based perovskites (LaMO 3), where on-site Coulomb interactions have been addressed by an additional Hubbard-type term. Calculated results indicate that with the exception of LaFeO 3 , the oxygen vacancy formation energy (Δ E f o r m a t i o n , v a c ) of LaMO 3 (M = Sc - Cu) becomes less positive when moving across the first transition metal period. The first four LaMO 3 perovskites have very high oxygen vacancy formation energies and can hardly be reduced under mild conditions, while the other five perovskites exhibit a much greater reducibility. During the formation of the first oxygen vacancy in LaMO 3 (M = Mn - Cu), the nearest neighbor transition-metal cations serve as the primary acceptors of the electrons left behind. As oxygen atoms are further removed, square-based pyramidal and tetrahedral coordination geometries appear successively, and an abrupt increase in Δ E f o r m a t i o n , v a c is observed at a specific oxygen deficiency (δ), which defines the maximum possible δ in the perovskite structures. Under this definition, the M3+ cations (M = Mn - Ni) can be possibly reduced to M2+ while LaCuO 3 may lose at most one lattice oxygen atom per formula unit before it is deactivated. [ABSTRACT FROM AUTHOR]