The effects of hot-pressing (HP) and spark plasma sintering (SPS) methods on the grain size, microstructural features, and mechanical behaviour of graphene nanoplatelet/carbon nanotubes (GNTs) reinforced Al 2 O 3 nanocomposites were comprehensively studied. Different graphene nanoplatelet to carbon nanotube ratios were selected as the overall reinforcement content of composites prepared using HP and SPS. Highly densified samples (>98%) were obtained at 1650 °C under 40 MPa in Ar atmosphere, with dwell times of 1 h and 10 min for HP and SPS respectively. Both types of sample showed a mixture of inter- and transgranular fracture behaviour. A 50% grain size reduction was observed for samples prepared by HP compared to SPS samples. Both types of samples achieved a high flexural strength and fracture toughness of >400 MPa and 5.5 MPa m 1/2 , whilst SPS samples peaked at relatively lower GNT contents than those for the HP samples. Based on analyses of the morphology, grain sizes and fracture mode, similar toughening mechanisms for both types of sample were observed, involving the complex characteristics of the combined GNT fillers. [ABSTRACT FROM AUTHOR]

Abstract: This research explores the use of a variety of carbon nanostructures as reinforcing agents for Si3N4 matrix composites. We have chosen highly promising families of carbon materials: multiwall, singlewall carbon nanotubes (MWCNTs, SWCNTs), graphene, carbon black nanograins and graphite micrograins for use as fillers. These materials were dispersed with a concentration of 3wt% in silicon nitride matrices. A high efficiency attritor mill has also been used for effective dispersion of second phases in the matrix. In the present work the development of sintering processes (hot isostatic pressing (HIP) and spark plasma sintering (SPS)) has been performed to consolidate and tailor the microstructure of Carbon nanotube (CNT)-reinforced silicon nitride-based ceramic composites. The silicon nitride nanocomposite systems retained the mechanical robustness of the original systems. Elastic modulus measurements and micro-indentation investigations of the hardness and fracture toughness have been performed as well as scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction in order to characterize the composites produced by the two sintering methods. [Copyright &y& Elsevier]