Search

In this study, pure ZnO and iron (Fe) and cobalt (Co) co-doped ZnO nanoparticles were synthesized by varying Fe and Co concentrations using the co-precipitation method. The physical properties of as-prepared samples were investigated through XRD, FTIR, SEM, and UV–vis spectroscopy. X-ray diffraction confirmed the strong influence of Fe and Co ions on structural parameters without disturbing the basic ZnO hexagonal structure. The microstructural study was executed by using the Scherrer, W–H, and SSP methods. FTIR confirmed the presence of Zn–O, and Zn–M–O (M = Fe, Co) vibrational modes, which further confirmed the successful incorporation of dopants ions. The energy bandgap (E g) extracted from UV–vis spectra has shown red-shift (3.37–2.7 eV) for decreasing Fe contents, whereas blue-shift (3.37–3.39 eV) for increasing Co concentration. SEM was used to investigate surface morphology, which represents the high rate of agglomeration. The photocatalytic test was performed on grown samples against various dyes and also observed the effects of varying concentrations of Fe and Co ions. The maximum degradation efficiency (98.8%) at 6%Fe and 4%Co under direct sunlight in 60 min against methylene blue (MB) was achieved. The photocatalytic activity of optimized concentration (6%Fe and 4%Co) was further tested against cresol red (CR), methyl orange (MO), safranin-O (SO), rhodamine-B (RhB), and methyl red (MR) dyes. The maximum degradation efficiency against MR dye (96.0%) was observed. The antibacterial test against Staphylococcus aureus and Klebsiella pneumoniae bacterial strains have shown that co-doped ZnO nanoparticles have a higher activity as compared to pristine ZnO, and furthermore, the sample with 6%Fe and 4%Co concentration exposed the highest antibacterial actively for both bacterial strains. [ABSTRACT FROM AUTHOR]

Novel Zn 0 · 95 Mn 0 · 05 O and Zn 0 · 9 Mn 0.05 M 0.05 O (M = Al, Bi, Sr, Ag) nanocrystals were prepared via the co-precipitation technique. The X-ray diffraction pattern confirmed the substitution of Mn, Al, Bi, Sr, and Ag dopants without altering the basic ZnO structure. The microstructural study was performed by employing the Scherrer plot, Williamson-Hall, and SSP methods. The energy bandgap calculated from UV–vis spectra using different methods observed red-shifted by co-doping. The other optical parameters were also studied and discussed in detail. The FTIR spectra confirmed the presence of Zn–O, and Zn-M–O vibrational modes. Raman spectra demonstrated the presence of ZnO phonon modes, and the Raman shift exhibited the structural defects induced by dopants. The PL spectra showed strong NBE and DLE in the UV and visible region due to extrinsic defects. The IV measurements exhibited the enhancement in the electrical conductivity of ZnO by co-doping. The photocatalytic activity was performed under direct sunlight for methyl orange and methylene blue dyes, and the enhanced degradation efficiency was achieved by co-doping. Furthermore, this article enhances the understanding of tuning the physical properties of ZnO by co-doping and introduces a new class of sunlight-driven photocatalysts. [ABSTRACT FROM AUTHOR]

In this study, the micro-emulsion approach was adopted to fabricate rare earth (Nd) and transition metal (Cu) co-doped barium hexaferrite (Ba 1-x Nd x Fe 12-y Cu y O 19) nanoparticles (NPs). The fabricated co-doped and undoped materials were characterized by FTIR, XRD, and SEM techniques for structural and morphological investigation. Structural studies such as XRD and FTIR confirmed Nd and Cu doping at the tetrahedral and octahedral sites of barium hexaferrite, respectively. The SEM analysis made sure that the materials were successfully produced at the nanoscale. Dielectric measurements revealed that the dielectric constant and AC conductivity values of the co-doped sample were higher than those of the undoped sample. The VSM study confirms the improved magnetic properties of the sample after co-doping that facilitates its separation and reuse after photocatalytic experiments. The co-doped and undoped sample's photocatalytic activities (PCA) were explored by comparing their Methyl Green (MG) dye degradation efficiencies. The results revealed that the co-doped barium hexaferrite sample degraded almost 92.6% of the MG dye, while the undoped sample degraded just 37.4%. The higher PCA of the co-doped sample is credited to its structural defects, which adjust the band interval to increase electrical conductivity. In addition, the co-doped sample lost only 2% photocatalytic efficiency after five successive cycles, demonstrating its potential for reuse. Application studies have clearly shown that our Nd-Cu co-doped barium hexaferrite sample has a great potential for practical application to remove toxic dyes from the environment. [Display omitted] [ABSTRACT FROM AUTHOR]