Search

How to deal with the brittleness of ceramic materials is always one of the hot topics in the field of materials science. Design of layered ceramics with textured structure is one of the effective methods to improve their fracture toughness. The introduction of additives as interlayer phases can balance fracture toughness and flexural strength. However, the research about addition of interlayer phases and their mechanisms in the layered ceramics is still limited. In this work, nacre-like alumina ceramics were successfully fabricated by freeze casting followed by hot pressing. Silicon nitride was incorporated as the interlayer phase, and the effect on the mechanical properties of the nacre-like alumina was investigated. The addition of silicon nitride was beneficial to improvement of interlayer bonding between the alumina layers due to formation of sialon phase, leading to increase of flexural strength but decease of fracture toughness. When the content of silicon nitride was 3.3 wt%, flexural strength and fracture toughness of the sample was 468 MPa and 6.2 MPa m1/2, respectively. Compared with the sample without silicon nitride, the flexural strength was enhanced significantly. Additionally, both flexural strength and fracture toughness were improved as compared the sample without any additives. This work can provide available references for design and fabrication of high-strength and high-toughness ceramics by properly tuning the layer structure and interlayer phase composition. [ABSTRACT FROM AUTHOR]

Synergic effect of graphene oxide (GO) and silicon nitride whisker (Si 3 N 4 w) on the mechanical properties of nacre-like alumina was investigated in this study. A comprehensive analysis on the composites, including microstructure, relative densities, flexural strength and fracture toughness, was carried out. The experimental results showed that, GO promoted the fracture toughness of the composites, but reduced the flexural strength slightly; while adding a certain amount of Si 3 N 4 w improved both flexural strength and fracture toughness. With the incorporation of GO and Si 3 N 4 w, the highest flexural strength reached 520 MPa and the fracture toughness reached 9.59 MPa m1/2. Microstructure observation revealed that the enhanced mechanical properties were ascribed to the synergistic toughening mechanisms induced by the nacre-like structure of alumina, GO pull-out, Si 3 N 4 w pinning and pull-out. [ABSTRACT FROM AUTHOR]

Abstract Graphene oxide (GO) is one of the most important ceramic-toughening candidates due to its outstanding physical and chemical properties. In this paper, nacre-like alumina ceramics reinforced with GO have been prepared by freeze casting followed by hot pressing. The experimental results showed that a laminated structure with homogeneous distribution of GO was obtained in the composites. Microstructural analysis, relative densities, flexural strength and fracture toughness of the samples were investigated to reveal the effect of GO. Higher flexural strength and fracture toughness (~380 MPa and ~7.5 MPa m1/2, respectively) were achieved and the multiple length-scale toughening mechanisms of composites contributed to the improved mechanical properties. The results show that it is a promising method to enhance the mechanical properties of nacre-like alumina by the addition of GO. [ABSTRACT FROM AUTHOR]