Search

Abstract The mechanical strength of highly porous ceramic foams shows significant attenuation with the increase of porosity, especially for ceramic foams with very high porosity level above 95%. Ultra-light bulk composite ceramic foams were fabricated via introducing 20 wt% zirconia in alumina-based cell wall, aiming at improving mechanical strength of alumina based ceramic foams. The preparation and stability of alumina and zirconia particles synergistically stabilized foams were investigated. The obtained bulk ceramic foams manifested an exciting combination of both high porosity above 96% and excellent specific compressive strength, due to their closed pore structure, defect-free cell wall with uniform thickness, and uniformly distributed zirconia grains in alumina matrix. The alumina/zirconia composite ceramic foams with porosity of 96.7% exhibited compressive strength of 1.11 ± 0.07 MPa, which was much higher than that of alumina ceramic foams in the case of same porosity. [ABSTRACT FROM AUTHOR]

The generation of PVA hydrogel through freeze-thaw technique has been utilized innovatively to complete the forming process of porous Si 3 N 4 ceramics in the present work. In comparison with gelcasting method, green body with comparable strength has been achieved by this novel forming process, which is owing to the strong function of PVA gel caused by the freeze-thaw cycles. Herein, Si 3 N 4 hollow spheres are employed as pore-forming agent in order to achieve closed pores. The morphology of green body illustrates that pores originate from both hollow spheres and the space occupied by ice crystals, and the latter gives rise to the increase of porosity around 10%. Studies on the mechanical, dielectric and thermal properties of porous Si 3 N 4 ceramics dependent on freeze-thaw cycle and freezing time have been performed. It is found that porous ceramics treated for freeze-thaw 2 cycles with freezing time of 24 h present excellent properties, which are promising to be applied as radome materials. [ABSTRACT FROM AUTHOR]

Abstract A facile method for preparation of SiC nanofibrous network reinforced hierarchical structured porous Si 3 N 4 based ceramics via annealing Si-Si 3 N 4 binary particle-stabilized foam in coke bed is reported in this work for the first time. The atmosphere created by coke bed enables the fabrication of Si 3 N 4 based porous ceramics at 1450 °C without using sintering additives. As prepared specimens possess a relative high compressive strength due to the partial oxidation of Si 3 N 4 particles. This novel structure with three levels of hierarchy characterized by flexible SiC nanofibrous network, cell walls and unit cells can be characterized. The vaporization of silicon powder results in formation of Si(g), SiO(g) and allows subsequent generation of SiC nanofibrous network, leading to a considerable number of micro-pores on cell walls simultaneously. As-prepared porous ceramics contained 76.7% porosity and had compressive strength of 10.81 MPa. [ABSTRACT FROM AUTHOR]

Mechanically robust alumina ceramics with low shrinkage were successfully prepared via gelcasting using Isobam as the gelling agent and pre-sintered alumina powder as the raw material for the first time. The influence of amount of pre-sintered alumina powder and powder's pre-sintering temperature on the viscosity of suspension and mechanical properties of low-shrinkage alumina ceramics were systematically investigated. The results showed that low-shrinkage alumina ceramics with flexural strength of 294.5 ± 33.0 MPa, linear shrinkage of 7.79% and relative density of 91.5% can be obtained with the addition of 60 wt% alumina powder pre-sintered at 1600 °C. This convenient and facile approach is promising to fabricate low-shrinkage alumina ceramics with large sizes, high dimensional accuracy and complex shapes. [ABSTRACT FROM AUTHOR]