Search

Reported here is a systematical investigation on the crystal structure, magnetic properties and magnetocaloric (MC) effect of three rare earth (RE) molybdate RE 2 MoO 6 (RE = Dy, Tb and Gd) oxides. The X-ray powder diffraction and the morphology as examined using the scanning electron microscope indicate phase-pure and polycrystalline nature of these oxides. The temperature (2–100 K) and magnetic field (up to 5 T) dependence of the magnetic measurements determine the magnetic phase transition (MPT) and MC properties. All the present RE 2 MoO 6 oxides crystallize in a monoclinic structure belonging to C 2/ c space group with the antiferromagnetic ordering at low temperature. Moreover, the RE 2 MoO 6 oxides hold reasonable values of MC parameters including the maximum isothermal magnetic entropy change/temperature-averaged entropy change (2 K lift) and relative cooling power values have been evaluated with the magnetic change of 0–5 T, yielding 17.22 (17.08) J/kgK and 277.67 J/kg for Dy 2 MoO 6 , 17.03 (16.83) J/kgK and 261.12 J/kg for Tb 2 MoO 6 , as well as 27.68 (26.69) J/kgK and 228.14 J/kg for Gd 2 MoO 6 , respectively. These acceptable MC parameters make the present RE 2 MoO 6 oxides potential candidates for cryogenic magnetic refrigeration (MR). [ABSTRACT FROM AUTHOR]

In this paper, a detailed investigation with respect to the structural, cryogenic magnetic properties and magnetocaloric performances of RE 2 CuMnO 6 (RE = Gd, Dy, Ho and Er) double perovskite (DP) compounds has been performed. All the RE 2 CuMnO 6 compounds are confirmed to B -site disordered and crystallized in the GdFeO 3 -type structure (Pnma space group, N 62, oP20). The magnetic transition temperatures (T M) are found to be ~7.5 K for Gd 2 CuMnO 6 , ~12.1 K for Dy 2 CuMnO 6 , ~12.2 K for Ho 2 CuMnO 6 , and ~3.6 K for Er 2 CuMnO 6 , respectively. Moreover, for checking the magnetocaloric performances several vital parameters including -Δ S M max (peak value of magnetic entropy change, -Δ S M), TEC (3) (temperature averaged -Δ S M) and RCP (relative cooling powers) are evaluated to be 7.84, 7.73 J/kgK and 151.1 J/kg for Gd 2 CuMnO 6 , 5.69, 5.59 J/kgK and 180.9 J/kg for Dy 2 CuMnO 6 , 7.12, 7.05 J/kgK and 192.4 J/kg for Ho 2 CuMnO 6 , as well as 9.92, 9.60 J/kgK and 195.9 J/kg for Er 2 CuMnO 6 under the magnetic field change Δ H = 5 T, respectively. [ABSTRACT FROM AUTHOR]

In this work, we fabricated the RE 2 O 2 SO 4 (RE = Gd, Tb, Dy and Ho) oxides by thermal decomposition and systematically determined regarding their structural and magnetic properties, especially of the magnetic phase transition (MPT) and magnetocaloric effect (MCE). All of these RE 2 O 2 SO 4 oxides are confirmed to crystallize in an orthogonal structure (space group: pmnb); the constituting elements are all distributed uniformly and presented as the RE 3+, S6+, and O2− valence states, respectively. They all exhibit a typical cryogenic MPT from paramagnetic to antiferromagnetic (AFM) state together with a field-induced metamagnetic transition (first-order type MPT) from AFM to ferromagnetic state below their MPT temperatures. All of these RE 2 O 2 SO 4 oxides exhibit considerable direct and inverse cryogenic MCE. The determined direct magnetocaloric parameters of present RE 2 O 2 SO 4 oxides, especially of Gd 2 O 2 SO 4 and Ho 2 O 2 SO 4 oxides, are comparable with most of recently reported RE -based magnetic solids, making them also considerable for practical cryogenic MR applications. [ABSTRACT FROM AUTHOR]

We herein investigated four rare earth (RE)-based oxides, the RE 2 SiO 5 (RE = Gd, Dy, Ho, and Er) silicates, regarding their structural and cryogenic magnetic properties. All the RE 2 SiO 5 silicates are found to crystallized in a monoclinic structure. X-ray photoemission spectroscopy spectra illustrate that RE , Si and O elements in RE 2 SiO 5 silicates are present as RE 3+, Si4+, and O2−, respectively. The Dy 2 SiO 5 reveals a first-order magnetic transition around 4.5 K. The magnetic phase transition temperatures are probably below 2 K for the RE 2 SiO 5 (RE = Gd, Ho, and Er) silicates. Large cryogenic magnetocaloric effects (MCE) and good magnetocaloric performances were observed in the RE 2 SiO 5 silicates. The MCE parameters in terms of the maximum magnetic entropy changes, the temperature-averaged entropy change (5 K-lift) and refrigerant capacity under a magnetic field change of 0–5 T are determined to be 35.5, 30.4 J/kgK, and 215.7 J/kg for Gd 2 SiO 5 , to be 13.3, 12.9 J/kgK, and 190.5 J/kg for Dy 2 SiO 5 , to be 15.3, 15.1 J/kgK, and 274.1 J/kg for Ho 2 SiO 5 and to be 17.9, 16.5 J/kgK, and 181.14 J/kg for Er 2 SiO 5 , respectively. These derived values of MCE parameters of the RE 2 SiO 5 silicates, especially for Gd 2 SiO 5 , are at similarly high level with or better than those of the updated candidate materials, making them also of potential for practical magnetic refrigeration applications. [ABSTRACT FROM AUTHOR]

The magnetic refrigeration (MR) based on magnetocaloric effect (MCE) is a key technique, since it possesses ideally higher performance than the traditional gas compression technology. However, the lack of MR materials with excellent MCE performance is a bottle-neck for practical MR applications. Herein, we systematically report the structural properties using powder X-ray diffraction and scanning electron microscope as well as the magnetic and magnetocaloric properties through the magnetization measurements of four rare-earth (RE) ruthenate RE 3 RuO 7 (RE = Pr, Nd, Gd and Tb) compounds. Light RE -based Pr 3 RuO 7 and Nd 3 RuO 7 compounds form an orthorhombic Cmcm structure, while heavy RE based Gd 3 RuO 7 and Tb 3 RuO 7 compounds crystallize in an orthorhombic P 2 1 nb structure. The magnetic phase transition of all the present compounds are confirmed to be of the first-order type with T N of 52, 15, 11 and 12 K for Pr 3 RuO 7 , Nd 3 RuO 7 , Gd 3 RuO 7 and Tb 3 RuO 7 compounds, respectively. The related MCE parameters including the maximum isothermal magnetic entropy change, temperature-averaged entropy change (5 K lift), and refrigerant capacity with the magnetic field change of 0–5 T were computed to be 1.35 J/kgK, 1.31 J/kgK, and 27.4 J/kg for Pr 3 RuO 7 , to be 2.18 J/kgK, 2.04 J/kgK, and 25.6 J/kg for Nd 3 RuO 7 , to be 8.12 J/kgK, 7.90 J/kgK, and 124.6 J/kg for Gd 3 RuO 7 , and to be 7.78 J/kgK, 7.49 J/kgK, and 128.8 J/kg for Tb 3 RuO 7 , respectively. [ABSTRACT FROM AUTHOR]

The crystal structure, microstructure, magnetic phase transitions and magnetocaloric effect (MCE) in KNaSnF6-type GdCrWO 6 and ErCrWO 6 oxides have been investigated. Both GdCrWO 6 and ErCrWO 6 oxides are confirmed to crystalize in a polar aeschynite type structure with the space group of Pna 2 1 (No.33, oP36). The grain size remains relatively average according to the SEM graph. Under low magnetic field of 0.1 T, the ErCrWO 6 oxide undergoes two successive magnetic transitions around 22 and 7 K, whereas only a weak magnetic transition around 6 K can be noticed. The paramagnetic Curie temperatures θ p are fitted to be −17.0 and −16.6 K for GdCrWO 6 and ErCrWO 6 oxides, respectively, suggesting that the antiferromagnetic (AFM) interaction is dominant at ground state. With the magnetic field change (ΔH) of 0–7 T, the peak value of magnetic entropy change (-ΔS M), refrigeration capacity (RC), relative cooling power (RCP) and 5 K lift temperature-averaged ΔS M (TEC) are figured to be 9.13 J/kg-K, 152 J/kg, 190 J/kg and 9.07 J/kg-K for GdCrWO 6 as well as to be 5.3 J/kg-K, 128 J/kg, 161 J/kg and 5.09 J/kg-K for ErCrWO 6 , respectively. The MCE parameters for GdCrWO 6 and ErCrWO 6 oxides are comparable with recently reported RE -based MCE oxides, indicating present GdCrWO 6 and ErCrWO 6 oxides also considerable for cryogenic magnetic refrigeration (MR). [ABSTRACT FROM AUTHOR]