Pyrochlore Nd 2 Zr 2 O 7 nanoparticles were prepared by complex-precipitation in aqueous media, followed by calcination in MgO matrix and subsequent dissolution processing. A suite of characterization techniques, including X-ray diffraction, Raman, TEM, SEM, dynamic light scattering, and nitrogen sorption, was employed to investigate the structure and particle size of the synthesized nano materials. Results show that calcination at 1200 °C for 20 h forms Nd 2 Zr 2 O 7 with pyrochlore structure. The matrix phase (MgO) had no effect on the formation of pyrochlore phase. The MgO phase was readily removed by dissolution at 0.5 M HNO 3 aqueous solution; and the remaining pyrochlore Nd 2 Zr 2 O 7 nanoparticles had a diameter of approximately 200 nm estimated by TEM and approximately 550 nm determined by light scattering due to slight aggregation. The bulk density of the pelletized powder reached approximately 99% of theoretical value, after uniaxial pressing at 2.0–2.5 MPa and sintering at 1400 °C for 48 h. [ABSTRACT FROM AUTHOR]

A novel soft chemistry route was developed to synthesize Y 2 Hf x Ti 2− x O 7 (0≤ x ≤2.0) oxide solid solution. An aqueous solution containing reactants was produced to ensure the combustion reaction taking place at the molecular level. A suite of characterization techniques, including X-ray diffraction, Raman, transmission electron spectroscopy, as well as X-ray absorption near edge structure (XANES), is employed to investigate the structural and phase changes of the series. Both X-ray and electron diffraction patterns show that the Y 2 Hf x Ti 2− x O 7 system undergoes a clear composition-induced phase transition from ordered pyrochlore to disordered defect-fluorite at x ~1.5. On the other hand, Raman and XANES spectra reveal a gradual evolution of the local structure with the substitution of Hf for Ti. [ABSTRACT FROM AUTHOR]

Abstract: Pyrochlore structured Nd2Sn x Zr2−x O7 (x=0–2) ceramics were prepared by a new chemical synthesis route in an aqueous media. Raman spectra and X-ray diffraction patterns confirmed the formation of the pyrochlore structure after sintering at 1400°C. SEM results showed pelletized materials became dense with increasing Zr/Sn mole ratio and sintering temperature. These candidate materials have characteristic structures for the development of nuclear waste forms or inert matrix nuclear fuels. [Copyright &y& Elsevier]