In order to study the variation of rare earth oxides during thermal failure of thermal barrier coatings, Eu2O3-doped YSZ coatings with 0.5 mol%, 1.0 mol% and 1.5 mol% were prepared by explosive spraying. SEM, XRD, EDS and microhardness tester were used to analyze the effect of different rare earth oxide doping content on the morphology, composition and mechanical properties of the coatings. The results showed that with the increase of rare earth oxide doping content, the porosity of the coatings decreased, and the microhardness and fracture toughness increased. When the doping amount of rare earth oxide is 1.0 mol%, the bonding strength and thermal cycle times of the coating are the highest, 33.4 Mpa and 185 times respectively. With the increase of the doping amount of rare earth, the luminous intensity of the sprayed coating increases. After thermal shock test, the luminous intensity of Eu2O3-doped YSZ coatings at 592 and 608 nm decreased to a certain extent.

In order to improve the erosion resistance and toughness of thermal barrier coatings, YSZ coatings, 20 vol%-AlBOw whisker modified YSZ coatings and 20 vol%-BNw whisker modified YSZ coatings were prepared by plasma spraying. The cross-section structure, morphology, composition and phase composition of coatings and powders were analyzed by SEM, EDS and XRD. The erosion resistance of three coatings was tested by self-made erosion tester. The crack growth resistance of coatings was tested and calculated by Vickers hardness tester. The results show that the density of the coating is improved by adding AlBOw and BNw. The whisker inhibits the crack propagation through the mechanisms of crack deflection, whisker pull-out and whisker bridging. The addition of whisker improves the erosion resistance of YSZ coating by 8.17% and 13.94%, which can effectively improve the service life of thermal barrier coating.

To enhance the fracture toughness and thermal shock resistance of the thermal barrier coatings (TBCs), detonation spraying has been used to prepare modified neodymium (Ⅲ) oxide (Nd2O3)-doped yttria-stabilized zirconia (YSZ) TBCs containing 20 vol% (D1 coating) and 30 vol% (D2 coating) of boron nitride whiskers (BNws). Analyses were performed using a scanning electron microscope (SEM), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), and a microhardness tester to examine the manner in which the doping content of different rare earth oxides affected the coating morphology, composition, and mechanical properties. The results denoted that the porosity of the D2 coating was 47.9% higher than that of the D1 coating; the whisker content was 30 vol% in the former and 20 vol% in the latter. The increased porosity reduced the microhardness and bond strength of the coating. However, the fracture toughness (KIC) of the D2 coating was increased to 2.67 MPa·m1/2 because the whisker content was 8.5% higher than that in the D1 coating. The thermal cycling life of the D2 coating was 245 cycles, and its thermal shock resistance was 9.9% higher when compared with that of the D1 coating. A TBC with better overall performance was obtained when BNw reached 30 vol%.