Carbon spheres, prepared by hydrothermally treating fresh potato starch, is employed as the sulfur host to configure a high-performance cathode substrate candidate for Li–S batteries. As confirmed by experimental results, both the improved the rate and cycle performances of Li–S batteries cathode with gradient sulfur immobilization, are mainly attributed to the confining, adsorption and conduction multi-functions of as-prepared carbon spheres toward polysulfides. Specifically, on starting the discharging/charging cycles, the active material α-S8 is irreversibly converted to polysulfides and then transformed between β-S8 and polysulfides during the next charge/discharge cycles. After initialization at 0.1C for 3 cycles, the initial reversible discharge capacities of the Li–S batteries cathode with optimized sulfur amount are 1072.5, 831.3, 780.4, 726.8, 714.3, 702.7 mAh g−1sulfur at 0.1, 0.5, 1, 2, 3 and 4 C, which is superior to those of the most previously reported reports. Besides that, as-designed potato-derived carbon based composite cathodes exhibits remarkable rate performance and cycling stability even at wide temperature ranging from −40 to 60 °C, which evidently supports the dominant role of as-prepared 3D carbon spheres in boosting the cathode performance for Li–S batteries.

In this study, we have successfully coated the CeO2 nanoparticles (CeONPs) layer onto the surface of the Ni-rich layered LiNi0.7Co0.2Mn0.1O2 cathode materials by a wet chemical method, which can effectively improve the structural stability of electrode. The X-ray powder diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), and X-ray photoelectron spectroscopy (XPS) are used to determine the structure, morphology, elemental composition and electronic state of pristine and surface modified LiNi0.7Co0.2Mn0.1O2. The electrochemical testing indicates that the 0.3 mol% CeO2-coated LiNi0.7Co0.2Mn0.1O2 demonstrates excellent cycling capability and rate performance, the discharge specific capacity is 161.7 mA h g−1 with the capacity retention of 86.42% after 100 cycles at a current rate of 0.5 C, compared to 135.7 mA h g−1 and 70.64% for bare LiNi0.7Co0.2Mn0.1O2, respectively. Even at 5 C, the discharge specific capacity is still up to 137.1 mA h g−1 with the capacity retention of 69.0%, while the NCM only delivers 95.5 mA h g−1 with the capacity retention of 46.6%. The outstanding electrochemical performance is assigned to the excellent oxidation capacity of CeO2 which can oxidize Ni2+ to Ni3+ and Mn3+ to Mn4+ with the result that suppress the occurrence of Li+/Ni2+ mixing and phase transmission. Furthermore, CeO2 coating layer can protect the structure to avoid the occurrence of side reaction. The CeO2-coated composite with enhanced structural stability, cycling capability and rate performance is a promising cathode material candidate for lithium-ion battery.