Search

Selective catalytic reduction of NOx by ammonia (NH3‐SCR) was affected by HCl, which was widely present in industrial flue gas. In this study, the SCR performances over MOx‐WO3/TiO2 (MW/Ti, M=Mn, Ce and V) catalysts after HCl treatment were investigated. It was found that HCl poisoning showed inhibition and promotion in NOx conversion over MnW/Ti and CeW/Ti catalysts, respectively. While the SCR activity over VW/Ti catalyst was hardly affected by HCl. Over MnW/Ti catalyst, the rupture of the Mn−O bond by the strong Mn−Cl binding induced the formation of amorphous MnCl2 species. This Cl‐containing species with Mn in a low oxidation state exhibited poorer redox ability and NO activation, resulting in a decrease in low‐temperature SCR activity. However, instead of directly affecting the CeOx and VOx sites, gaseous HCl reacted with NH3 to form NH4Cl species on the surface of CeW/Ti and VW/Ti catalysts. As a result, the SCR activity of VW/Ti catalyst was scarcely influenced by HCl, taking the unchanged redox ability and NH3 adsorption. With a further accumulation of NH4Cl on CeW/Ti catalyst, the NOx conversion at low temperature was evidently enhanced due to the promotion in NO‐to‐NO2 conversion (Fast‐SCR). [ABSTRACT FROM AUTHOR]

Selective catalytic reduction of NOx by ammonia (NH3‐SCR) was affected by HCl, which was widely present in industrial flue gas. In this study, the SCR performances over MOx‐WO3/TiO2 (MW/Ti, M=Mn, Ce and V) catalysts after HCl treatment were investigated. It was found that HCl poisoning showed inhibition and promotion in NOx conversion over MnW/Ti and CeW/Ti catalysts, respectively. While the SCR activity over VW/Ti catalyst was hardly affected by HCl. Over MnW/Ti catalyst, the rupture of the Mn−O bond by the strong Mn−Cl binding induced the formation of amorphous MnCl2 species. This Cl‐containing species with Mn in a low oxidation state exhibited poorer redox ability and NO activation, resulting in a decrease in low‐temperature SCR activity. However, instead of directly affecting the CeOx and VOx sites, gaseous HCl reacted with NH3 to form NH4Cl species on the surface of CeW/Ti and VW/Ti catalysts. As a result, the SCR activity of VW/Ti catalyst was scarcely influenced by HCl, taking the unchanged redox ability and NH3 adsorption. With a further accumulation of NH4Cl on CeW/Ti catalyst, the NOx conversion at low temperature was evidently enhanced due to the promotion in NO‐to‐NO2 conversion (Fast‐SCR). [ABSTRACT FROM AUTHOR]

Abstract: Copper‐exchanged H‐SAPO‐47 zeolites were synthesized by an aqueous solution ion exchange method and applied in the selective catalytic reduction of NO with NH3 (SCR). The microporous chabazite (CHA) structure of the catalysts was characterized and confirmed using synchrotron X‐ray diffraction and nitrogen adsorption–desorption experiments. The synthesized Cux‐SAPO‐47 catalysts exhibited excellent SCR activity and nearly 100 % N2 selectivity in a wide temperature range. The Cu0.1‐SAPO‐47 sample exhibited higher activity than the other samples below 250 °C. The weak Lewis acid sites originating from the introduction of Cu2+ were more active than the Brønsted acid sites of the zeolites framework at low temperature. Two types of isolated Cu2+ species with different coordination surroundings were found, namely, Cu2+ cations bonded with the six‐membered rings and those bonded in the CHA cages. The former species exhibited good stability and activity at high temperature, whereas the latter ones were more active at low temperature. The Cu0.1‐SAPO‐47 catalyst provided a considerable amount of isolated Cu2+ bonded in the CHA cages. These results indicated that active Lewis acid sites and isolated Cu2+ species are responsible for their excellent SCR activity. [ABSTRACT FROM AUTHOR]