Search

A novel method, Thermally Modified Non-Solvent Induced Phase Separation (T-NIPS) has been developed to fabricate translucent hollow fiber (THF) photocatalytic membrane for membrane's photodegradation efficiency enhancement. The process involves two-step temperature treatment that attacks crystalline property of polyvinylidene fluoride (PVDF). Graphitic carbon nitride in a modified morphological structure (hollow nanofiber) was used as photocatalyst to investigate the effect of translucency on membrane's photodegradation efficiency. UV-Vis analysis coupled with FTIR highlighted different crystalline phase appearance and membrane's translucency. The membranes showed high translucency, ranging from 60.0% to 93.9%, with THF-PVDF/PVP-GCN (2.0) exhibiting the highest. The filtration experiment showed that membrane with GCN photocatalyst had high PWF (1200 L/m2h) and rejection (90%) OPW compared to neat THF-PVDFs. In suspended mode, GCN demonstrated an impressive photodegradation efficiency of 99.98%. When immobilized in opaque PVDF membrane, the photodegradation has decreased substantially to 49.40%. However, when immobilized in a translucent PVDF membrane, the photodegradation efficiency of HN-GCN significantly improved compared to the opaque PVDF membrane, reaching 95%. Translucent membrane was subjected to five cycle regeneration test and showed 90% recovery even after the fifth cycle. The 10% reduction in the recovery was investigated using FESEM analysis revealed that there is a cake layer formation on the membrane surface. Therefore, this study proved that translucency of membrane has significant effect on immobilized photocatalyst's photocatalytic efficiency. [Display omitted] • Novel T-NIPS method to produce THFM is developed. • HN-GCN successfully immobilized in THFM. • HN-GCN immobilized THFM showed increased degradation efficiency of OPW. [ABSTRACT FROM AUTHOR]

This study involves the preparation of a double-skinned thin film composite (TFC) and thin film nanocomposite (TFN) hollow fiber (HF) membrane for forward osmosis (FO) applications. The porous substrate consisted of a Polyvinyl chloride (PVC) / Polycarbonate (PC) blend HF membrane. Interfacial polymerization (IP) was then applied to coat a polyamide (PA) layer on the lumen surface and the porous substrate's outer surface. In addition, the impact of the outer PA active layer and the addition of nanoparticles to the outer selective layer on the FO flux and internal concentration polarization (ICP) were studied. By adding the second active layer to the substrate, water flux, reverse salt flux and ICP decreased. Also, the decline of water flux decreased over time due to the fouling agent. To compensate for the decrease in water flux in the double-skinned membrane, graphene oxide (GO) nanoparticles with 0.05% and 0.1%wt were added to the outer active layer. Addition of 0.1%wt graphene oxide nanoparticle to the outer active layer can help to improve water flux about 78% without spoiling the reverse salt flux. Moreover, the performance of double-skinned membranes against osmotic dilution process for oily wastewater treatment was investigated. The findings of this study demonstrated that the novel double-skinned TFN HF membrane exhibited high FO performance with low ICP and fouling. [Display omitted] • Inclusion of a second active layer without reducing the reverse salt flux and fouling. • To improve fouling resistance of membrane, GO was added to second active layer. • By adding GO to outer active layer, reverse salt flux and fouling was reduced. • The Hermia model showed intermediate blocking in neat membrane. • The predominant fouling in double-skin membranes is cake formation. [ABSTRACT FROM AUTHOR]