The objective of the study was to investigate the relationship between pH-neutralization, hydrophilicity, and free hygroscopic expansion stress of self-adhesive resin cements (SARCs) after storage in artificial saliva. The SARCs RelyX Unicem Automix 2 (RX2, 3 M ESPE), iCEM (iCEM, Heraeus) and Maxcem Elite (MCE, Kerr) were under investigation in this study. Cylinders (height × diameter, 6 × 4mm) were prepared from each material and stored in artificial saliva (7d at 37 °C). Cylinder height was measured at baseline and after 7 days. After storage, the compression modulus was measured to calculate the free hygroscopic expansion stress. For pH-neutralization and hydrophilicity assessment, disks (height × diameter, 1 × 1.5 mm) were prepared, covered with electrolyte, and monitored over 24 h at 37 °C. Hydrophilicity was assessed using the static sessile drop technique at baseline and at different time intervals up to 24 h. Data were analyzed using one-way ANOVA and post hoc Student-Newman-Keuls test (S-N-K, α = 0.05). After 24 h, RX2 (pH24h 4.68) had a significantly higher (p

The aim of the present study was evaluate the effect of microparticulate silver additions in adhesives on secondary caries formation using an artificial mouth model. One hundred eight intact human third molars received standardized Class-V resin composite restorations (Filtek Supreme XTE bonded with Syntac, Scotchbond 1 XT, Futurabond M). Adhesives were charged with different amounts of microparticulate silver (0 %/0.1 %/0.5 %). After storage for 4 weeks at 37 °C, teeth were subjected to 10,000 thermocycles (+5 °C and +55 °C), and impressions were taken. Streptococcus mutans 10449 was used in a nutrition medium for secondary caries simulation in a fully automated artificial mouth. After completion of thermocycling and biological load cycling, impressions were taken and replicas were investigated under a light microscope for gap widths at enamel and dentin margins. Evaluation of fluorescence was carried out using a special FITC filter. The demineralization depths at the cavity margin were evaluated using Xpert for Windows working at a pixel distance of 5 μm. After thermocycling, no difference in gap widths and demineralization depths was found (p > 0.05). After incubation, gap widths and demineralization depths were significantly reduced with higher amounts of silver loading in most of the adhesives (p