Recent technological development of utilizing an active screen made of solid carbon for plasma-assisted thermochemical diffusion treatments opens up new possibilities for control over the in situ generated treatment environment to guarantee reproducible treatment conditions and material responses. Until now, the investigations of active-screen plasma nitrocarburizing (ASPNC) using an active screen manufactured from solid carbon focused on the influence of a single treatment parameter variation on the material response. In this systematic study, experiments were conducted to vary the H2-N2 feed-gas composition while varying the bias plasma power. The experiments served to better understand a simultaneous variation in the mentioned parameters on the resulting treatment environment and material response during ASPNC of AISI 316L austenitic stainless steel. Therefore, nitriding and carburizing effects in the expanded austenite layer can be obtained. It is shown that an increased nitriding effect, i.e., nitrogen diffusion depth and content, was achieved in case of biased conditions and for H2-N2 feed-gas compositions with higher N2 amounts. On the contrary, an increased carburizing effect, i.e., carbon diffusion depth and content, was achieved in nonbiased conditions, independent from the H2-N2 feed-gas composition. [ABSTRACT FROM AUTHOR]

Active screen plasma nitrocarburizing (ASPNC) increases the surface hardness and lifetime of austenitic stainless steel without deteriorating its corrosion resistance. Using an active screen made of carbon opens up new technological possibilities that have not been exploited to date. In this study, the effect of screen power variation without bias application on resulting concentrations of process gas species and surface modification of AISI 316L steel was studied. The concentrations of gas species (e.g., HCN, NH3, CH4, C2H2) were measured as functions of the active screen power and the feed gas composition at constant temperature using in situ infrared laser absorption spectroscopy. At constant precursor gas composition, the decrease in active screen power led to a decrease in both the concentrations of the detected molecules and the diffusion depths of nitrogen and carbon. Depending on the gas mixture, a threshold of the active screen power was found above which no changes in the expanded austenite layer thickness were measured. The use of a heating independent of the screen power offers an additional parameter for optimizing the ASPNC process in addition to changes in the feed gas composition and the bias power. In this way, an advanced process control can be established. [ABSTRACT FROM AUTHOR]