Search

Bimetallic metal-organic frameworks (MOFs) with a controlled morphology are potential materials for boosting the electrochemical performance of supercapacitors owing to their unique structural merits. Herein, a solvent-regulated strategy was proposed to synthesize bimetallic MOFs with various morphologies, such as microflowers, microspheres, and nanosheets, and the possible mechanisms of morphology control during nucleation and crystal growth were analyzed. When employed as electrode materials for supercapacitors, the NiCo-MOF microflowers possessed the biggest specific capacitance, which could achieve 1086 F g−1 at a current density of 1 A g−1. To further improve the electrochemical performance of materials, NiCo-P was prepared via a low-temperature phosphating method using NiCo-MOF microflowers as the precursor. Electrochemical studies displayed that the NiCo-P(6) microflowers exhibited good capacitance and superior rate capability with specific capacitances of 1592 and 1384 F g−1 at 1 and 20 A g−1, respectively. Furthermore, an asymmetric supercapacitor assembled by NiCo-P(6) and active carbon exhibited a high energy density of 51.2 Wh kg−1 at a power density of 749.8 W kg−1 and outstanding cycling stability. This work is easy to operate and can be extended to the preparation of other MOF-based electrode materials. The delivered excellent electrochemical performance suggests the resulted flower-like NiCo-P is a promising electrode material for advanced energy storage devices. [Display omitted] [ABSTRACT FROM AUTHOR]

As a typical pseudocapacitance material, NiS is considered a promising electrode material due to its high theoretical specific capacitance and abundant reserves. However, the electrical conductivity is poor, resulting in a decrease in cycle stability and rate performance. Here, we introduce cobalt-containing porous nanocarbon (Co-NC) derived from zeolite-imidazolate frameworks (ZIFs) as a supporting base to design a hybrid structure. As an electrode material, NiS@Co-NC nanocomposite has a composite effect of double-layer capacitive porous carbon and pseudo-capacitance NiS nanoparticles and excellent electrochemical performance. Specifically, the specific capacitance of NiS@Co-NC nanocomposite is as high as 1116.6 F·g−1 when the current density is 1 A·g−1, and capacity retention is 90.177% at a very high current density of 10 A·g−1 after 5000 cycles. Moreover, the fabricated hybrid supercapacitor delivers an energy density of 21.6 Wh·kg−1 at 799.9 W·kg−1 with coulombic efficiency of 90.177%, and 14.22 Wh·kg−1 at a high power density of 7999.9 W·kg−1, along with excellent cyclic stability of 89.85% at 5 A·g−1 after 5000 cycles. All results indicate that NiS@Co-NC nanocomposites have the potential to be applied as electrodes in hybrid supercapacitors and other energy storage devices. ZIF-67 @ZIF-8 was synthesized through hydrothermal reaction and carbonized as a sacrificial template to generate cobalt-containing nano-carbon and carbon nanotubes. [Display omitted] • CNTs interconnected NiS@Co-containing porous carbon nanocomposite was synthesized. • The composite showed a strong synergistic effect of NiS, CNTs and metallic cobalt modified porous carbon. • NiS@Co-NC nanocomposite has a high specific capacitance of 1116.6 F.g-1 1 A.g-1. [ABSTRACT FROM AUTHOR]

Due to the insufficient performance, it is still a challenge to combine conventionally synthesized metal-organic framework (MOF-74) with other materials to fabricate composite electrodes for high-performance supercapacitors. Herein, we synthesized a series of NiCo-MOF-74 composite materials with different amounts of polypyrrole nanotubes (T-PPy) denoted as NiCo-MOF-74/T-PPy-m (m = 2.5, 5, 10, 15 and 20) through in situ growth of the bimetallic MOF around the PPy nanotubes by a simple solvothermal method. By comparison, the NiCo-MOF-74(1)/T-PPy-10 composite, with a Ni/Co molar ratio of 1:1 obtained in the presence of 10 mg of T-PPy, possessed the highest specific capacitance of 849 C·g−1 at 1 A·g−1 and excellent cyclic stability with a capacitance retention rate of 90.0% after 10,000 cycles as well as good rate performance. Moreover, the assembled asymmetric supercapacitor respectively using NiCo-MOF-74(1)/T-PPy-10 and active carbon as positive electrode and negative electrode achieved a superior energy density of 58.4 Wh kg−1 at the power density of 747.6 W kg−1 and high cyclic lifespan (91.4% capacitance retention after 10,000 cycles). The mechanism of capacitance increase was studied in detail, influences of metal molar ratios, morphology and addition amounts of PPy on electrochemical performances of the formed composition materials were systematically discussed, and it was found that the interpenetrating network structure assembled by "string of candied haws"-like T-PPy-interweaved NiCo-MOF-74(1) polyhedrons possessed the best capacitive performance for enhanced conductivity of the resulted composite, improved dispersity of the bimetallic MOF and more exposed active sites. And the interwoven structure alleviated the stress change-induced structure or phase variation caused by repeated volumetric swelling and shrinking during charge/discharge cycle and enhanced the rate capability and cycling stability. Interpenetrating network structure assembled by "string of candied haws"-like T-PPY-interweaved NiCo-MOF-74(1) polyhedrons [Display omitted] • Interpenetrating networks assembled by PPY nanotube-interweaved NiCo-MOF-74 were constructed. • The structure delivered good conductivity, high specific capactitance and long cyclic lifespan as supercapacitor electrode. • NiCo-MOF-74 in situ grown around the PPY tubes was directly used as electrode without carbonization and heteroatom doping. [ABSTRACT FROM AUTHOR]

In this paper, novel hybrid nanomaterials constituting carbonized biomass materials derived from walnut shells and metal-organic framework (MOF) have been researched as a new class of renewable supercapacitor materials for electrochemical energy storage. One synthetic route is employed to grow Ni-MOF in the peripheries and channels of walnut shells derived carbon (WS), which had been carbonized previously by heat treatment in air at 850 °C to produce a highly porous network, and vulcanized polyaniline (SPANI) is used as a dummy plate preventing the agglomeration of MOFs and a wire connecting WS and MOFs, which easily improves the electron transfer and enhances the conductivity of the electrode material. The specific capacitance of the obtained WS@Ni-MOF composite is up to 4 times that of the biochar at the current density of 1 A g-1. The connection of SPANI also obviously accelerates the transfer of electrolyte ions. The resulting specific capacitance could reach 14 times of the biochar and exhibit high cycle stability (retention rate of 90.4% after 20000 cycles). In addition, the assembled asymmetrical supercapacitor (ASC) shows a high energy density of 34.79 Wh kg-1 at the power density of 824 W kg-1. This work provides a brilliant renewable candidate for the excellent energy storage device and a promising route design strategy for preparation of high performance and long life electrode materials. [Display omitted] • Design and fabrication of self-assembled Walnut shell-derived carbon and MOF composites. • WS@Ni-MOF/SPANI, as a new electrode material with sandwich structure, applied for supercapacitors for the first time. • The specific capacitance of WS@Ni-MOF/SPANI is greater than that of WS, Ni-MOF and SPANI. • Excellent cyclic stability of WS@Ni-MOF/SPANI (90.4%@20000). [ABSTRACT FROM AUTHOR]

[Display omitted] • MoS 2 @Ni-MOF was prepared and alkalized to obtain MoS 2 /Ni(OH) 2. • MoS 2 /Ni(OH) 2 has high specific capacitance and long cycling life for supercapacitor. • MoS 2 /Ni(OH) 2 was used to construct electrochemical sensor for HQ and CC. A nickel-based metal-organic framework (Ni-MOF) layer was in situ grown on the surface of the sheet MoS 2 to synthesize MoS 2 @Ni-MOF as a precursor. In order to improve the properties of the precursor material, the final MoS 2 /Ni(OH) 2 material was obtained by alkalizing the precursor material. Supercapacitors and electrochemical sensors were prepared by MoS 2 /Ni(OH) 2 composite material. The test indicates that alkaline treatment of Ni-MOF materials is helpful to improve electrochemical performance. MoS 2 /Ni(OH) 2 material used as supercapacitor electrode has a high specific capacitance of 2192 F g−1 and excellent cyclic stability (the capacitance retention rate remains 85.19% after 10,000 charge/discharge cycles). The hybrid supercapacitor (HSC) was assembled with MoS 2 /Ni(OH) 2 as the positive electrode and activated carbon as the negative electrode. The MoS 2 /Ni(OH) 2 //AC HSC device shows an excellent energy density of 50.58 Wh kg−1 at the power density of 800 W·Kg−1. In addition, the MoS 2 /Ni(OH) 2 modified GCE electrode is an excellent electrochemical sensor for the simultaneous determination of hydroquinone (HQ) and catechol (CC). The modified electrode provides wide linear ranges of 1 ∼ 500 and 2 ∼ 400 μM and low detection limits of 0.43 and 0.48 μM for HQ and CC, respectively (S/N=3). The MoS 2 /Ni(OH) 2 material can be applied to supercapacitors and electrochemical sensors, indicating that the material has great potential application value in energy storage and biosensing. [ABSTRACT FROM AUTHOR]

• The novel Mn-Ni double hydroxide composite was prepared by alkalizing the Mn/Ni-MOF-74 precursor. • MnNiDH shows high specific capacitance and excellent retention rate. • The assembled aqueous and all-solid-state devices display high energy densities and wide voltage window. MOF-derived hydroxides provide a promising platform for high performance supercapacitors as electrode materials. Herein, a novel manganese-nickel double hydroxide (MnNiDH) composite with special morphology has been successfully prepared by alkalizing the precursor Mn/Ni-MOF-74. Obtaining electrode material inherits the spear-shaped morphology of the precursor well and possesses a smaller particle size by potassium hydroxide treatment. The smaller particle size and rich microporous structure can shorten the ion or proton transport path, thereby improve its electrochemical activity and utilization. Benefiting from these specific properties, the resultant MnNiDH composite demonstrates a high specific capacitance of 2498 F g−1 at a current density of 1A g−1. The assembled aqueous device exhibits high energy density of 58.53Wh kg−1, meanwhile the all-solid-state device also displays energy density of 30.63 Wh kg−1 based on the outstanding voltage window of 0∼2.1 V. These results suggest that as-synthesized MnNiDH hold great potential for practical applications in the energy storage field. [ABSTRACT FROM AUTHOR]

A facile alkaline treatment stripping precursor strategy is developed for preparing MOF derived double hydroxide. The bimetallic MOFs material provides multi-type of redox reaction centres, and the hydroxide nanonanoflower obtained by alkali stripping Ni-MOF@Co-MOF effectively expands the "active area (circumference)" of the redox reaction. The exfoliated sheets expose more active sites, which are more favorable for effective contact with the electrolyte and facilitate the occurrence of redox reactions. The MOF derived double hydroxide maintains the structural and performance advantage of the MOF precursor as well as overcomes the disadvantages of poor conductivity and serious agglomeration of common hydroxide. As-synthesized electrode exhibited high specific capacity of 1088 C g−1 at 1 A g−1 and cycle retention of 94% after 12,000 cycles. Furthermore, assembled battery-supercapacitor hybrid device exhibits a maximum energy density of 66.5 Wh kg−1 at a power density of 825 W kg−1, and superior cycle retention and coulombic efficiency of 86% and 95% after 18,000 cycles, which shows that Ni-MOF@Co-MOF derived double hydroxide has good potential application value. [ABSTRACT FROM AUTHOR]