The failure mode is a dominant factor of mechanical performance of braided composite tube subjected to axial compression. The failure mode was modified by tailoring stack-up sequence of composite tubes hybridized by bi/tri-axial braided laminate. The thermal photographing and micro-CT scanning methods were employed to monitor the in-situ damage progression and post-mortem specimen, respectively. The results show that the delamination was easy to be induced at the interface nearby tri-axial braided laminate. It attributes to the combination between the crack caused by local buckling of the axial yarns and the crack caused by shear deformation of braiding yarns. By the illumination of this behavior, delamination is controlled to occur at the different position along thickness direction of braided tube by adjusting the stacking sequence of braided laminates. When delamination position transfer from the inner/outer sides to the middle of tube wall, the failure mode transfer from the progressive folding to splaying, which increase the specific energy absorption by 45.77%. [ABSTRACT FROM AUTHOR]

• The usage of correlation between maximum temperature and peak load. • The reconstruction of CT images identifies the debonding distribution and degree. • A novel inspection way of combing infrared imaging and micro CT reconstruction methods. • The role of axial yarns in axial crushing. In this work, the effect of axial yarns on damage behavior of two-dimensional triaxially braided composite(2DTBC) tubes subjected to axial compression was investigated. A novel damage detection method combining infrared thermography and CT scanning was presented. In the area without axial yarns, yarn crossovers were separated from each other due to interlacing patterns. Axial compression caused the braiding yarns to shear deformation like scissors. Inter-yarn de-bonding appeared in crossovers and could not connect. Consequently, it caused a progressively folding failure mode. In contrast, local buckling occurred on axial yarns because of their primary loading behavior. Cracks along the axial yarns formed, which would combine with debonding crossovers caused by the sheared braiding yarn. It resulted in significant inter-layer delamination and consequently splaying failure mode. The energy absorption of composites tube with 18 axial yarns increased by 79.9% at the cost of 27.8% fiber usage more than 3 axial yarns. [ABSTRACT FROM AUTHOR]