Search

• There are coupling effects between fatigue and environmental corrosion actions. • Transportation models of harmful substances in the concrete accounting for fatigue damage. • Physical damage of freeze–thaw cycles and sulphate attack decrease fatigue life. • Multiple alternated simulation test is a potential way to study combined effect of fatigue and corrosion. When in use, reinforced concrete bridge structures not only experience high-frequency fatigue loading caused by passing vehicles, but also suffer from the effects of a corrosive environment. In addition to fatigue damage to reinforcement, long-term fatigue loading also causes concrete cracking and deterioration of pore structures, thereby accelerating the ingress of external corrosive substances and reducing concrete durability. Long-term exposure to a corrosive environment also reduces the performance of concrete and causes corrosion of reinforcement materials, affecting the fatigue performance of the structure. Therefore, there is a combined effect between fatigue loads and corrosion on concrete. This paper is a review of the current literature from a material perspective on the performance degradation of concrete under the combined action of fatigue loading and corrosion, that is, carbonation, chloride ion attack, freeze–thaw cycles, and sulphate attack. The paper includes (1) a description of a test method for examining the combined action of fatigue loading and corrosion, (2) a summary of performance degradation of concrete under the combined effect of fatigue loading and corrosion, and (3) an introduction to durability deterioration models considering fatigue damage, and fatigue models that can account for corrosion. Finally, potential future research on concrete under the combined effect of fatigue loading and corrosion is described. [ABSTRACT FROM AUTHOR]

• Frost resistance of concrete exposed to E-FTCs worsen with the decrease in pre-curing time. • Subsequent curing conditions after E-FTCs significantly affects the later-age frost resistance of the damaged concrete. • There are good correlations between the parameters of the damage model and the pre-curing strengths of damaged concrete. • Prediction models of freeze–thaw damage suitable for damaged concrete exposed to E-FTCs are created. • For concrete expected to experience E-FTCs, adequate pre-curing strength and re-curing conditions are essential. Concrete subjected to freeze–thaw cycles action at early-age will suffer serious physical damage, resulting in degradation of the concrete's performance. The subsequent curing conditions after early-age freeze–thaw cycles (E-FTCs) are critical to the development of the properties of frost-damaged concrete. Four test environments were set up for this study, based on different numbers of E-FTCs and subsequent curing conditions. The later-age resistance to freeze–thaw of concrete exposed to E-FTCs was evaluated by analysing the influence of pre-curing times and curing conditions. Results show that the earlier the FTCs occur, the worse the later-age freeze–thaw resistance is. In particular, for the frost-damaged concrete with a pre-curing time of 18 h, its freeze–thaw resistance is significantly worse than that of other concretes that have a longer pre-curing time. The increase in the number of E-FTCs exacerbates the damage to early-age concrete, which causes the reduced later-age freeze–thaw resistance. Subsequent water curing can significantly improve the freeze–thaw resistance of damaged concrete, while air curing is the least effective. Based on previous freeze–thaw damage models, prediction models for concrete exposed to E-FTCs were created by using the test data obtained in this study. The critical pre-curing strengths which can ensure that the damaged concrete has satisfactory frost resistance at later-age were thus obtained. For concrete structures expected to experience E-FTCs, adequate pre-curing strength and good re-curing conditions are essential. [ABSTRACT FROM AUTHOR]

This research studies the influences of pre-curing time, the number and environment of early-age freeze–thaw damage (E-FTD) and later-age curing methods on later-age performance of concrete subjected to E-FTD. The concrete specimens with pre-curing time of 18 h, 24 h, 48 h and 72 h were subjected to four different E-FTD systems. Subsequently, three later-age curing methods were performed to the time of 28 days respectively and finally the later-age compressive strength, resistance to chloride penetration and freeze–thaw of concrete were evaluated. The results show that all three later-age performance indexes improve gradually as the pre-curing time prolongs. The damage of the salt freeze–thaw environment to early-age concrete is severer than that of the water freeze–thaw environment, resulting in the unsatisfactory later-age performance even with restorative curing. Among all later-age curing methods, the restoration effect of water curing on later-age performance is the best. Compared to the standard curing, the restoration effect of natural air curing on later-age compressive strength and resistance to chloride penetration of concrete is better, but that on resistance to freeze–thaw is worse. For the concrete with shorter pre-curing time, the recovery percentage of durability indexes, especially the resistance to freeze–thaw, is always lower than that of compressive strength. The pre-curing time should be prolonged appropriately for the early-age freeze–thaw damaged concrete with the requirement of durability. [ABSTRACT FROM AUTHOR]