A series of high quality x%Pr3+:BaF2 (x = 0.6, 1, 2); (1%Pr3+, 2%Na+):BaF2; (1%Pr3+, y%Ca2+):BaF2 (y = 3, 5) and (0.6%Pr3+, 10%R3+):BaF2 (R = Y, Lu, Gd) crystals were grown by temperature gradient technique (TGT). The Raman spectra, absorption spectra, fluorescence spectra, and fluorescence decay lifetime were measured. XRD patterns indicate that the as-synthesized samples are pure BaF2 phase. The absorption cross-section of Pr3+ ions in the BaF2 matrix can be greatly improved by co-doping R3+ ions, while improvement by Na+ and Ca2+ ions is marginal. The fluorescence characteristic of Pr3+ ions can be effectively regulated by co-doping Na+, Ca2+, R3+ (R = Y, Lu, Gd) ions of different valence states. When R3+ ions are introduced, the fluorescence spectra show the strongest orange emission and the CIE chromaticity coordinates of Pr3+ ions are also in the orange region. When single-doped Pr3+ ions and Na+ or Ca2+ ions are introduced, the fluorescence lifetime of the 3P0 level is double exponential decay, and the short lifetime is the main proportion. However, the fluorescence centers tend to homogeneous and stable by R3+ ions co-doping and the fluorescence lifetime exhibits single-exponential decay, which is fitted to 49.7 μs, 47.8 μs and 49.6 μs of (0.6%Pr3+, 10%R3+):BaF2 (R = Y, Lu, Gd), respectively. All the results show that (Pr3+, Gd3+):BaF2 and (Pr3+, Na+):BaF2 are excellent laser gain media for high-efficiency orange and red laser operation. [ABSTRACT FROM AUTHOR]

A series of Ce-doped YAG-Al2O3 eutectics were grown by the micro-pulling-down (μ-PD) method, for the purpose of high power white light emitting diodes. The eutectic structure was investigated. A calibrated integrating sphere spectrometer setup was used to measure the white LED properties of eutectic samples. The CIE color coordinates can be regulated easily by altering the Ce3+ doping concentration and sample thickness of the Ce:YAG-Al2O3 eutectics. A 1 W white LED device based on Ce:YAG-Al2O3 eutectics at a rated current of 350 mA emitted a bright white light with a CIE coordinate of (0.319, 0.334), a luminous efficacy of 83.0 lm W−1 and a Duv value of 0.003. The results showed that Ce:YAG-Al2O3 eutectics have better luminescence properties than commercial powder phosphors at a high current density. [ABSTRACT FROM AUTHOR]