Search

Objective The aim of the present study was to assess the effect of water storage on the quasi-static properties and cyclic fatigue behavior of four contemporary CAD/CAM resin composite materials. Methods The CAD/CAM resin composites Grandio Blocs, LavaTM Ultimate, CerasmartTM and Brilliant Crios, as well as the direct resin composite Grandio SO, were evaluated. Rectangular plates were cut from the blocks or fabricated using a silicon mold to obtain specimens for fracture toughness (KIc, n = 10), biaxial strength (σ0, n = 30) and cyclic fatigue testing (n = 30). Half of the specimens was stored for 24 h in dry conditions and the other half was aged for 60 days in distilled water at 37 °C. KIc was determined using the Compact-Tension (C(T)) method and σ0 and cyclic fatigue were tested using the Ball-on-Three-Balls assembly. Additional disc-shaped specimens (n = 5) were produced to obtain water sorption curves of the materials. Weibull statistics and two-way ANOVA with Tukey’s post-hoc test were used for data assessment. Results The highest water sorption was observed for LavaTM Ultimate (42.6 μg/mm3), whereas Grandio SO displayed the lowest uptake (14 μg/mm3). A statistically significant drop in KIc and σ0 was measured for all materials after water storage, except for the σ0 of CerasmartTM. Water ageing had a dissimilar effect on the cyclic fatigue behavior, increasing the slow crack growth susceptibility of LavaTM Ultimate, but decreasing it for CerasmartTM and Brilliant Crios. Significance Contemporary CAD/CAM resin composites are susceptible to water driven degradative processes, although differences in filler content and resin matrix constitution play an important role in how it impacts their mechanical properties.

Here we use the 3-point bending with eccentric notch test (3-PBEN) to investigate the fracture behavior of a pressable and a CAD/CAM lithium disilicate (LS2) glass-ceramics under combined mode-I and mode-II loading. The effect of the bulk texturization in the beams of the pressable LS2 is made visible through the fracture trajectory following the most energetically favorable path dictated by the crystallite alignment. The CAD/CAM LS2 shows an isotropic fracture mode but increasing fracture energy with mode-II contribution, similar to the pressable variant.

Objective Strength is one of the preferred parameters used in dentistry for determining clinical indication of dental restoratives. However, small dimensions of CAD/CAM blocks limit reliable measurements with standardized uniaxial bending tests. The objective of this study was to introduce the ball-on-three-ball (B3B) biaxial strength test for dental for small CAD/CAM block in the context of the size effect on strength predicted by the Weibull theory. Methods Eight representative chairside CAD/CAM materials ranging from polycrystalline zirconia (e.max ZirCAD, Ivoclar-Vivadent), reinforced glasses (Vitablocs Mark II, VITA; Empress CAD, Ivoclar-Vivadent) and glass-ceramics (e.max CAD, Ivoclar-Vivadent; Suprinity, VITA; Celtra Duo, Dentsply) to hybrid materials (Enamic, VITA; Lava Ultimate, 3M ESPE) have been selected. Specimens were prepared with highly polished surfaces in rectangular plate (12 × 12 × 1.2 mm3) or round disc (O = 12 mm, thickness = 1.2 mm) geometries. Specimens were tested using the B3B assembly and the biaxial strength was determined using calculations derived from finite element analyses of the respective stress fields. Size effects on strength were determined based on results from 4-point-bending specimens. Results A good agreement was found between the biaxial strength results for the different geometries (plates vs. discs) using the B3B test. Strength values ranged from 110.9 MPa (Vitablocs Mark II) to 1303.21 MPa (e.max ZirCAD). The strength dependency on specimen size was demonstrated through the calculated effective volume/surface. Significance The B3B test has shown to be a reliable and simple method for determining the biaxial strength restorative materials supplied as small CAD/CAM blocks. A flexible solution was made available for the B3B test in the rectangular plate geometry.

Objectives The present study evaluated the effect of the coefficient of thermal expansion (CTE) mismatch and the cooling protocol on the distribution of residual stresses and crack propagation in veneered zirconia bilayers. Methods Ceramic discs with two different CTEs (Vita VM9 and Lava Ceram) were fired onto zirconia plates and cooled following a slow (0.5 °C/s) or a fast (45 °C/s) cooling protocol. The residual stress distribution throughout the veneer thickness was assessed by means of depth-wise Vickers indentation after sequentially sectioning the bilayers parallel compared to normal to the interface. A mathematical solution for the residual stress distribution was used as reference. Additionally, Hertzian cone crack propagation in the veneers was induced by cyclic contact loading and measured at different number of cycles to estimate the crack growth rate. Results The higher CTE mismatch of the VM9 group generated an important stress gradient with high compressive residual stresses near the interface, hindering the crack propagation. The low CTE mismatch group (Lava Ceram) developed only a slight stress gradient and higher cone crack growth rates. No differences were observed between the two cooling protocols applied regarding stress magnitude and crack propagation behavior. Significance The CTE mismatch has a predominant role in the generation of residual stress gradients within the veneer, which directly influences contact-induced crack propagation. Based on the results, the cooling protocol had no significant effect on the residual stress distribution in zirconia-veneer bilayers.