Search

Resin-ceramic hybrid materials for computer-aided design/computer-aided manufacturing (CAD/CAM resins) have been developed. In this study, the effects of the amount of light energy transmitted through the four types of 1.5-mm-thick CAD/CAM resin blocks on the bond performance of corresponding resin cement adhesive systems consisting of an adhesive and a dual-curable resin cement were examined. The bond strengths of the four types of resin cement adhesive systems decreased with decreasing the amount of light energy transmitted through CAD/CAM resin block, due to a decrease in the light-curable ability of dual-curable resin cements. However, the degradation behavior of the bond strengths was strongly affected by the types of adhesives and initiator systems utilized. The adhesive consisting of a dimethacrylate monomer and redox-initiators enhanced the bonding performance of the dual-curable resin cement more effectively than the adhesive, which consists of a dimethacrylate monomer and photo-initiators or a γ-me thacryloxypropyltrimethoxysilane and a 10-methacryloyloxydecyl dihydrogen phosphate.

In this study, effects of the degree of dissociation of acids on the hydrolysis rate of methoxy group in γ-methacryloxypropyltrimethoxysilane (γ-MPS) and the adsorption characteristics of γ-MPS on ceramic surfaces were studied using acetic, phosphoric, and hydrochloric acids. Hydrolytic stability of γ-MPS adsorption layer at the resin-ceramic interface was thus examined. (29)Si NMR observations of acidactivated γ-MPS and contact angle measurements following ceramic surface silanization were performed. Bond strengths of resin to the silanized ceramic surfaces were measured. Statistical analyses of shear bond strength and contact angle data were performed. Increase in the degree of dissociation of the acid used increased the hydrolysis rate of methoxy group in γ-MPS, but lowered the contact angle to the silanized ceramic surface. Decrease in the contact angle increased the hydrolytic stability of γ-MPS adsorption layer.

We designed three experimental 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based one-step (EX) adhesives consisting of MDP, urethane dimethacrylate, and triethylene glycol dimethacrylate adhesives with different water contents (98.4, 196.8, and 294.4 mg/g), and 4-methacryloyloxyethyl trimellitic anhydride (4-META) or 2-hydroxyethyl methacrylate (HEMA)-containing onestep adhesive. The effect of the amount of MDP-calcium (MDP-Ca) salt produced through demineralization of enamel and dentin on the bonding performance was examined. The efficacy of 4-META and HEMA was then discussed. When the amount of water in EX adhesive was increased, the production amount of MDP-Ca salt of enamel increased, but not the dentin. The enamel bond strength slightly increased with increasing the production amount of MDP-Ca salt, in contrast to the dentin. However, addition of 4-META in the EX adhesive (water content=98.4 mg/g) increased both bond strengths, although the production amounts of MDP-Ca salt significantly decreased. The 4-META enhances both bond strengths more effectively than the HEMA.

This study examined the effects on the bond durability of resins arising from the application of adhesive agent on porcelain surface, silanated by a ceramic primer consisting of gamma-methacryloxypropyltrimethoxysilane (gamma-MPTS), by comparing shear bond strengths before and after thermocycling. When an adhesive agent was applied to a porcelain surface which had been silanated by a ceramic primer for 10 seconds, a significant reduction in resin bonding durability was observed. Extending the silanating period of the ceramic primer to 60 minutes resulted in an increase in resin bonding durability to the porcelain surface. However, the effect on resin bonding durability resulting from the application of adhesive agent was nearly the same as that without adhesive agent application, even though the porcelain surface was silanated for 60 minutes. In other words, positive effects arising from adhesive agent application on resin bonding durability were not observed.

Three experimental self-etching primers - consisting of N-methacryloyl-omega-aminoalkyl phosphonic acid (NMomegaP) with different methylene chain lengths and N-methacryloyl glycine (NMGly) - were formulated. The influence of methylene chain length in NMomegaP derivatives on the chemical nature of calcium salts was examined following their application to tooth components. Bond strengths of experimental self-etching primers created with these monomers to enamel and dentin were also investigated. Nuclear magnetic resonance spectroscopy showed that NMomegaPs decalcified tooth components with formation of calcium salts, which changed from calcium hydrogen phosphonate to calcium phosphonate with increase in methylene chain length within the NMomegaP structure. Disparity in calcium salt formation was related to increases in bond strength to enamel from 18 to 24 MPa. However, bond strength to dentin remained unchanged (22 MPa). The relative dependency of bond strength on monomer methylene chain length was probably attributable to the sites where these NMomegaP calcium salts had deposited on the bonding substrates.

We designed self-etching primers consisting of a series of four N-methacryloyl-omega-amino acids, MomegaA, of different methylene chain numbers for resin core construction. The interacted amount of MomegaA's carboxylic acid with root or crown dentin apatite was determined, and its effects on dentin bond durability examined. The addition of both dentin particles to the MomegaA solutions caused the carbonyl carbon peak of carboxylic acid in MomegaA to shift to a lower field, chiefly because of an acid-base interaction between carboxylic acid and calcium. Then, as the pKa value of MomegaA's carboxylic acid increased, the amount of carboxylic acid that interacted with calcium decreased. In terms of dentin bonding durability, the four tested MomegaA adhesives provided noticeably higher bond strengths of resin to root or crown dentin than ED Primer II. Therefore, from the perspective of restoring pulpless teeth with minimal intervention, carboxylated MomegaA adhesives seemed to be very useful as functional monomers for self-etching primers.

Using finite element method (FEM), this study sought to investigate how the thickness and Young's modulus of cortical bone influenced stress distribution in bone surrounding a dental implant. The finite element implant-bone model consisted of a titanium abutment, a titanium fixture, a gold alloy retaining screw, cancellous bone, and cortical bone. The results showed that von Mises equivalent stress was at its maximum in the cortical bone surrounding dental implant. Upon investigation, it was found that maximum von Mises equivalent stress in bone decreased as cortical bone thickness increased. On the other hand, maximum von Mises equivalent stress in bone increased as Young's modulus of cortical bone increased. In conclusion, it was confirmed that von Mises equivalent stress was sensitive to the thickness and Young's modulus of cortical bone.