Search

There is a growing need for a mouthguard sheet material with higher shock absorption and dispersion capacity than those obtained by conventional materials. A five-layer mouthguard sheet material was previously developed using laminated ethylene vinyl acetate and polyolefin copolymer resin. In this study, the shock absorption capacity and dispersion capability of the new sheet material were investigated and compared with those of other materials. Impact testing for the new sheet material showed that the force required to displace the sheet by 1 mm was significantly higher at all thicknesses (p<0.001), whereas the puncture energy and displacement were significantly lower than those for ethylene vinyl acetate (p<0.05). The five-layer mouthguard sheet material successfully absorbed and resisted shock. Therefore, the sheet material potentially increases resistance to applied deformation in teeth and alveolar bone and maintains structure. The five-layer sheet material could expand the range of mouthguard products and help prevent oral trauma. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the application of fiberglass reinforcement method in thermoplastic mouthguard materials to improve flexural properties and adhesive strength. Commonly used two types of commercial mouth guard materials (ethylenevinyl acetate copolymer-based and polyolefin-based) were reinforced with glass fiber clothes by two-step hot press. Flexural strength and adhesive strength with each base material were examine via three-point bending test and delamination test, respectively. Ethylene-vinyl acetate copolymer-based fiberglass-reinforced material has significantly greater adhesive strength with base material and improvement of flexural properties compared with polyolefin-based material. These results suggest that flexural properties of both conventional commercial mouthguard materials were improved when the glass-fiber-reinforced method was applied to reinforce mouthguard materials, and more, ethylene-vinyl acetate copolymer was more desirable for the base material. [ABSTRACT FROM AUTHOR]

There is a growing need for a mouthguard sheet material with higher shock absorption and dispersion capacity than those obtained by conventional materials. A five-layer mouthguard sheet material was previously developed using laminated ethylene vinyl acetate and polyolefin copolymer resin. In this study, the shock absorption capacity and dispersion capability of the new sheet material were investigated and compared with those of other materials. Impact testing for the new sheet material showed that the force required to displace the sheet by 1 mm was significantly higher at all thicknesses (p<0.001), whereas the puncture energy and displacement were significantly lower than those for ethylene vinyl acetate (p<0.05). The five-layer mouthguard sheet material successfully absorbed and resisted shock. Therefore, the sheet material potentially increases resistance to applied deformation in teeth and alveolar bone and maintains structure. The five-layer sheet material could expand the range of mouthguard products and help prevent oral trauma.

The purpose of the present study was to develop an antibacterial mouthguard (MG) material using a masterbatch of silvernanoparticle--embedded ethylene-vinyl acetate (EVA) copolymers. In order to verify that the testing material was clinically applicable as an antibacterial MG material, we conducted an antibacterial test, a shock absorption test, and analysis of in vitro silver release. The colony-forming activity of Streptococcus sobrinus, Porphyromonas gingivalis, and Escherichia coli were significantly inhibited on the testing materials compared with the commercial EVA sheet (p<0.05). The shock absorption capability of the testing material was not significantly different from that of the commercial EVA sheet. Cumulative silver release (in pure water) from the testing materials were infinitesimal after soaking for 20 days, which implied that there could be no harm in wearing the MG during exercise. These results showed that this testing material could be clinically applicable as an antibacterial MG material. [ABSTRACT FROM AUTHOR]

The purposes of this study were to examine the shock absorption capability of addition-cured silicone denture relining materials and the bonding strength of addition-cured silicone denture relining materials and a commercial mouthguard material to determine its applicability to mouthguard adjustment. Two addition-cured silicone denture relining materials and eleven commercial mouthguard materials were selected as test materials. The impact test was applied by a free-falling steel ball. On the other hand, bonding strength was determined by a delamination test. After prepared surface treatments using acrylic resin on MG sheet surface, 2 types of addition-cured silicone denture relining materials were glued to MG surface. The peak intensity, the time to peak intensity from the onset of the transmitted force and bonding strength were statistically analyzed using ANOVA and Tukey's honest significant difference post hoc test (p<0.05). These results suggest that the silicone denture relining materials could be clinically applicable as a mouthguard adjustment material. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the application of fiberglass reinforcement method in thermoplastic mouthguard materials to improve flexural properties and adhesive strength. Commonly used two types of commercial mouth guard materials (ethylene-vinyl acetate copolymer-based and polyolefin-based) were reinforced with glass fiber clothes by two-step hot press. Flexural strength and adhesive strength with each base material were examine via three-point bending test and delamination test, respectively. Ethylene-vinyl acetate copolymer-based fiberglass-reinforced material has significantly greater adhesive strength with base material and improvement of flexural properties compared with polyolefin-based material. These results suggest that flexural properties of both conventional commercial mouthguard materials were improved when the glass-fiber-reinforced method was applied to reinforce mouthguard materials, and more, ethylene-vinyl acetate copolymer was more desirable for the base material.

The purpose of the present study was to develop an antibacterial mouthguard (MG) material using a masterbatch of silvernanoparticle-embedded ethylene-vinyl acetate (EVA) copolymers. In order to verify that the testing material was clinically applicable as an antibacterial MG material, we conducted an antibacterial test, a shock absorption test, and analysis of in vitro silver release. The colony-forming activity of Streptococcus sobrinus, Porphyromonas gingivalis, and Escherichia coli were significantly inhibited on the testing materials compared with the commercial EVA sheet (p<0.05). The shock absorption capability of the testing material was not significantly different from that of the commercial EVA sheet. Cumulative silver release (in pure water) from the testing materials were infinitesimal after soaking for 20 days, which implied that there could be no harm in wearing the MG during exercise. These results showed that this testing material could be clinically applicable as an antibacterial MG material.

We developed an ethylene vinyl acetate (EVA) containing surface pre-reacted glass-ionomer (S-PRG) filler, as a new mouthguard material for preventing intraoral bacterial infection. We examined its physical properties, antimicrobial activity against a major cariogenic bacterium Streptococcus mutans and a periodontopathogen Porphyromonas gingivalis, and its cytotoxicity toward human gingival epithelial cells. S-PRG filler was added to EVA copolymer at 5, 10, 20, or 40 wt% and was processed into disc-shaped test specimens. Only minor differences between the Shore hardness and rebound resilience properties of EVA materials with and without the S-PRG filler were observed. The specimens with S-PRG filler showed bacteriostatic activity toward S. mutans and P. gingivalis and inhibited S. mutans biofilm formation. No cytotoxicity against the gingival epithelial cells was observed. Our findings show that EVA containing S-PRG filler has antimicrobial activity toward pathogenic oral bacteria and may be an effective material for maintaining the oral health of athletes.