Search

Polyvinylidene fluoride (PVDF)/polytetrafluoroethylene (PTFE) hollow fiber membranes were developed via thermally induced phase separation (TIPS) method for direct contact membrane distillation (DCMD). The effects of PTFE addition on the thermal behavior of the dope mixtures and membrane formation were investigated. It was found that the crystallization of PVDF was significantly enhanced with increased nucleation sites provided by PTFE particles, leading to promoted formation of smaller spherulites in a greater density. Furthermore, the improved uniformity and increased amount of cavity between the spherical crystallites coherently facilitated the formation of smaller pores ranging from 0.08 to 0.12 μm. With certain PTFE loading, the membranes exhibited improved porosity, water permeability and hydrophobicity as well as enhanced tensile strength of 9.4 ± 0.3 MPa. To examine the DCMD performance, the membranes were tested under various conditions using 3.5 wt% NaCl solution. A stable permeation flux of 28.3 kg m − 2 h − 1 at the feed temperature of 60 °C with 99.99% NaCl rejection for over 50 h of operation was achieved, which is comparable with similar type of PVDF membranes while the newly developed membrane exhibited better mechanical strength. This study suggests that the as-spun PVDF/PTFE hollow fiber membranes have potential for DCMD applications. [ABSTRACT FROM AUTHOR]

The emerging technology of pressure retarded osmosis (PRO) has been intensely studied over the past decades due to its potential in harvesting salinity gradient energy, but membrane fouling can deteriorate the PRO performance. To mitigate membrane fouling, the outer surface of the inner-selective thin-film composite (TFC) polyetherimide (PEI) hollow fiber membrane was modified by depositing poly-(allylamine hydrochloride) (PAH) and poly acrylic acid (PAA) polyelectrolytes. The results show that the outer surface of the modified membrane had less pores exposed and was more negatively charged, which was beneficial for preventing the entrance and adsorption of the negatively charged foulants into the membrane substrate. It was further proved that the modified membrane was effective in reducing PRO fouling by organic macromolecules such as alginate and bovine serum albumin, while maintaining the mechanical properties and intrinsic separation properties well. Interestingly, after 200 ppm alginate was introduced to the feed water, the power density of the modified membrane could be maintained constant at 16.2 W·m − 2 at 15 bar while that of the non-modified membrane reduced around 17% at the end of a 300-min testing period. The results suggest that the polyelectrolytes deposition is a feasible strategy for adding anti-fouling property to PRO membranes. [ABSTRACT FROM AUTHOR]

This study investigated the fouling behavior and chemical cleaning of forward osmosis (FO) membranes for treating produced/process water (PPW) from a real gas field using thin-film composite FO hollow fiber membranes. Experiments revealed that membrane fouling occurred during the PPW treatment, which hindered the water and solute transport through the membrane. The water permeability and FO reference water flux of the membrane decreased by 22.9% and 24.8%, respectively, after fouling. Membrane surface characterization was carried out, and the results indicated the deposition and entrapment of organic species on the membrane after the PPW treatment. The efficiencies of various cleaning agents, including sodium dodecyl sulfate (SDS), ethylenediaminetetraacetic (EDTA) and NaOH, were evaluated. It was found that cleaning with SDS for 15 min is the most effective method for restoring water flux, and very stable FO performance can be obtained during batch treatment of PPW. The FO membrane can reduce the PPW volume by 50% at a relatively high average water flux of 15.6 L·m − 2 ·h − 1 in the active layer facing feed solution orientation using 1 M NaCl as draw solution (equivalent to the draw solution available in the field). This study demonstrates the great potential of FO technology for produced/process water treatment. [ABSTRACT FROM AUTHOR]

The ultra-permeable membranes (UPMs) are expected to reduce the specific energy consumption (SEC) of desalination, but the potential of UPMs in hollow fiber configuration has not been well quantified. Herein, we analyse the SEC and footprints of UPM modules in three feed salinities: seawater reverse osmosis (SWRO), brackish water RO (BWRO) and low-pressure RO (LPRO). Through the modelling the fluid dynamics and mass transport of RO systems, we find that a tripling in spiral-wound SWRO membrane permeability (based on the current value of 1 L m−2 h−1 bar−1; LMH/bar) could result in 16% decrease in SEC. Contrastingly, the quadrupling of hollow fiber SWRO membrane permeability (based on the current value of 0.25 LMH/bar) could reduce the SEC by 23%. According to our analysis, hollow fiber and spiral-wound SWRO membranes with permeabilities up to 1 LMH/bar and 3 LMH/bar, respectively, can reduce the SEC of seawater desalination. On the other hand, membranes with permeabilities up to 9 LMH/bar and 12 LMH/bar can lead to SEC savings in BWRO and LPRO desalination, respectively. This study provides a general guidance to RO membrane researchers on the permeability upper-limit of which UPMs could bring about SEC and footprint savings at a system level. [Display omitted] • Energy savings achievable by high permeability RO membranes were quantified. • Modelling was performed by simulating fluid dynamics in various RO configurations. • Hollow fiber SWRO membranes (up to 1 LMH/bar) could reduce energy consumption. • Spiral-wound SWRO membranes (up to 3 LMH/bar) could reduce energy consumption. • High permeability RO membranes could bring about greater benefits in BWRO/LPRO. [ABSTRACT FROM AUTHOR]

Abstract: The layer-by-layer (LBL) polyelectrolyte deposition was applied on polyethersulfone (PES) hollow fiber ultrafiltration membrane to prepare nanofiltration (NF) membrane for low pressure water softening application for the first time. The effects of polyelectrolyte type and molecular weight (MW), deposited bilayer number, polyelectrolyte solution pH and supporting electrolyte concentration on the performance of resultant membranes were studied thoroughly. Experiments revealed that the pH of the polyelectrolyte solution and supporting electrolyte concentration presented the most notable effects. For weak poly-cations, Poly(ethylenimine) (PEI) and Poly(allylamine hydrochloride) (PAH), the solution pH affected the membrane performance significantly, and high water permeability and divalent cation rejection were obtained at optimum pH values. Using a low concentration of supporting electrolyte at underneath layers was proved to be an effective way to increase water permeability while maintaining high salt rejection. A salt water flux (SWP) of 12LMH/bar and 94% Mg2+ rejection was obtained by depositing only two bilayers of PSS/PAH polyelectrolytes on the PES substrate, while for the 3000ppm mixed salt solution, the water permeability was 11LMH/bar with Mg2+ and Ca2+ rejection as high as 90%. These promising results demonstrate that LBL technique is potentially applicable for preparing low-pressure water softening hollow fiber membranes. [Copyright &y& Elsevier]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]