Search

Abstract: There has been a resurgence of interest in forward osmosis (FO) as a potential means of desalination, dewatering and in pressure retarded osmosis, which Sidney Loeb was advocating over 3decades ago. This paper describes the characteristics and potential applications of a newly developed FO hollow fiber membrane, which was fabricated by interfacial polymerization on the inner surface of a polyethersulfone (PES) hollow fiber. This FO membrane presents excellent intrinsic separation properties, with a water flux of 42.6L/m2 h using 0.5M NaCl as the draw solution and DI water as the feed with the active layer facing the draw solution orientation at 23°C. The corresponding ratio of salt flux to water flux was only 0.094g/L, which is superior to all other FO membranes reported in the open literature. To evaluate different application scenarios, various NaCl solutions (500ppm (8.6mM), 1wt.% (0.17M) and 3.5wt.% (0.59M)) were used as the feed water to test the performance of the FO membrane. The membrane can achieve a water flux of 12.4L/m2 h with 3.5wt.% NaCl solution as the feed and 2M NaCl as the draw solution, suggesting it has good potential for seawater desalination. [ABSTRACT FROM AUTHOR]

The emerging technology of pressure retarded osmosis (PRO) has been intensely studied over the past decades due to its potential in harvesting salinity gradient energy, but membrane fouling can deteriorate the PRO performance. To mitigate membrane fouling, the outer surface of the inner-selective thin-film composite (TFC) polyetherimide (PEI) hollow fiber membrane was modified by depositing poly-(allylamine hydrochloride) (PAH) and poly acrylic acid (PAA) polyelectrolytes. The results show that the outer surface of the modified membrane had less pores exposed and was more negatively charged, which was beneficial for preventing the entrance and adsorption of the negatively charged foulants into the membrane substrate. It was further proved that the modified membrane was effective in reducing PRO fouling by organic macromolecules such as alginate and bovine serum albumin, while maintaining the mechanical properties and intrinsic separation properties well. Interestingly, after 200 ppm alginate was introduced to the feed water, the power density of the modified membrane could be maintained constant at 16.2 W·m − 2 at 15 bar while that of the non-modified membrane reduced around 17% at the end of a 300-min testing period. The results suggest that the polyelectrolytes deposition is a feasible strategy for adding anti-fouling property to PRO membranes. [ABSTRACT FROM AUTHOR]

The ultra-permeable membranes (UPMs) are expected to reduce the specific energy consumption (SEC) of desalination, but the potential of UPMs in hollow fiber configuration has not been well quantified. Herein, we analyse the SEC and footprints of UPM modules in three feed salinities: seawater reverse osmosis (SWRO), brackish water RO (BWRO) and low-pressure RO (LPRO). Through the modelling the fluid dynamics and mass transport of RO systems, we find that a tripling in spiral-wound SWRO membrane permeability (based on the current value of 1 L m−2 h−1 bar−1; LMH/bar) could result in 16% decrease in SEC. Contrastingly, the quadrupling of hollow fiber SWRO membrane permeability (based on the current value of 0.25 LMH/bar) could reduce the SEC by 23%. According to our analysis, hollow fiber and spiral-wound SWRO membranes with permeabilities up to 1 LMH/bar and 3 LMH/bar, respectively, can reduce the SEC of seawater desalination. On the other hand, membranes with permeabilities up to 9 LMH/bar and 12 LMH/bar can lead to SEC savings in BWRO and LPRO desalination, respectively. This study provides a general guidance to RO membrane researchers on the permeability upper-limit of which UPMs could bring about SEC and footprint savings at a system level. [Display omitted] • Energy savings achievable by high permeability RO membranes were quantified. • Modelling was performed by simulating fluid dynamics in various RO configurations. • Hollow fiber SWRO membranes (up to 1 LMH/bar) could reduce energy consumption. • Spiral-wound SWRO membranes (up to 3 LMH/bar) could reduce energy consumption. • High permeability RO membranes could bring about greater benefits in BWRO/LPRO. [ABSTRACT FROM AUTHOR]